- 拉伸強度 [MPa]: 22.0
- 彎曲模量 [MPa]: 0.880
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Index of Compound | 10 g/10 min @Load 2.16 kg, Temperature 190 °C | 10 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 22.0 MPa | 3190 psi | ISO 527-2 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ISO 527-2 |
| Elongation at Break | 12 % | 12 % | ISO 527-2 |
| Flexural Modulus | 0.880 GPa | 128 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 167 °C | 333 °F | DSC |
| Vicat Softening Point | 147 °C @Load 1.02 kg | 297 °F @Load 2.25 lb | ISO 306 |