- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.22
- 拉伸強度 [MPa]: 26.0
- 熱變形溫度 [℃]: 125.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 50 mm/min |
| Elongation at Break | 8.0 % | 8.0 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min |
| Tensile Modulus | 3.12 GPa | 453 ksi | 1 mm/min |
| Charpy Impact Unnotched | 2.30 J/cm2 | 10.9 ft-lb/in2 | |
| 1.10 J/cm2 @Temperature -30.0 °C | 5.24 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.250 J/cm2 | 1.19 ft-lb/in2 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 163 °C | 325 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C | 163 °F | |
| Vicat Softening Point | 91.0 °C | 196 °F | 50°C/hr; 50N |