- 密度 [g/cm3]: 0.9
- 拉伸強度 [MPa]: 26.0
- 彎曲模量 [MPa]: 0.750
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in3 | ISO 1183 |
| Melt Index of Compound | 4.5 g/10 min @Load 2.16 kg, Temperature 230 °C | 4.5 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 615 % | 615 % | ASTM D638 |
| Flexural Modulus | 0.750 GPa | 109 ksi | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 162 °C | 324 °F | DSC |
| Vicat Softening Point | 137 °C | 279 °F | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 230 °C | 446 °F | |
| Adapter Temperature | 230 °C | 446 °F | |
| Die Temperature | 230 °C | 446 °F | |