- 密度 [g/cm3]: 1.24
- 缺口沖擊強(qiáng)度: 0.8
- 彎曲強(qiáng)度 [MPa]: 81.0
- 彎曲模量 [MPa]: 5.70
- 硬度: 107.0
- 熱變形溫度 [℃]: 161.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in3 | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 107 | 107 | ASTM D785 |
| Tensile Strength, Ultimate | 81.0 MPa | 11700 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| Flexural Modulus | 5.70 GPa | 827 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.63 J/cm | 6.80 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 161 °C | 322 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 229 - 246 °C | 444 - 475 °F | Approximate middle barrel temperature range |