- 密度 [g/cm3]: 1.3
- 缺口沖擊強度: 0.69
- 彎曲強度 [MPa]: 61.0
- 彎曲模量 [MPa]: 6.20
- 硬度: 107.0
- 熱變形溫度 [℃]: 159.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in3 | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 107 | 107 | ASTM D785 |
| Tensile Strength, Ultimate | 61.0 MPa | 8850 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 85.0 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.10 J/cm | 5.81 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 159 °C | 318 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C | 277 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 229 - 246 °C | 444 - 475 °F | Approximate middle barrel temperature range |