- 熔體流動速率 [g/10min]: 20.0
- 缺口沖擊強度: 1.8
- 拉伸強度 [MPa]: 22.0
- 彎曲模量 [MPa]: 0.990
- 熱變形溫度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ASTM D792 |
| Melt Flow | 20 g/10 min | 20 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Flexural Modulus | 0.990 GPa | 144 ksi | ASTM D790 |
| Izod Impact, Notched | 1.80 J/cm | 3.37 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 |
| UL RTI, Electrical | 115 °C | 239 °F | 0.030 in; UL 94 |
| Flammability, UL94 | V-2 @Thickness 1.57 mm | V-2 @Thickness 0.0618 in | |
| V-2 @Thickness 3.05 mm | V-2 @Thickness 0.120 in | ||