- 熔體流動速率 [g/10min]: 7.0
- 密度 [g/cm3]: 0.905
- 缺口沖擊強度: 0.427
- 拉伸強度 [MPa]: 25.0
- 彎曲模量 [MPa]: 1.20
- 硬度: 90.0
- 熱變形溫度 [℃]: 110.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | MD; ASTM D955 |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Tensile Modulus | 1.20 GPa | 174 ksi | ASTM D638 |
| Flexural Strength | 34.5 MPa | 5000 psi | ASTM D790 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.8 °C | 136 °F | |
| Flammability Test | 25 | 25 | FMVSS (mm/min) |