- 熔體流動速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.925
- 缺口沖擊強度: 0.448
- 拉伸強度 [MPa]: 39.0
- 彎曲模量 [MPa]: 1.700
- 硬度: 100.0
- 熱變形溫度 [℃]: 105.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | MD; ASTM D955 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | ASTM D638 |
| Tensile Modulus | 1.60 GPa | 232 ksi | ASTM D638 |
| Flexural Strength | 47.0 MPa | 6820 psi | ASTM D790 |
| Flexural Modulus | 1.700 GPa | 246.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.448 J/cm | 0.840 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.8 °C | 136 °F | |
| Flammability, UL94 | V-2 @Thickness 1.59 mm | V-2 @Thickness 0.0625 in | UL File #E99379(N) |