- 熔體流動速率 [g/10min]: 6.5
- 密度 [g/cm3]: 1.15
- 拉伸強度 [MPa]: 50.0
- 熱變形溫度 [℃]: 83.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in3 | |
| Moisture Absorption at Equilibrium | 0.30 % | 0.30 % | |
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm | 0.0065 in/in | |
| Melt Flow | 6.5 g/10 min @Load 3.80 kg, Temperature 230 °C | 6.5 g/10 min @Load 8.38 lb, Temperature 446 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | |
| Elongation at Break | 25 % | 25 % | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| Tensile Modulus | 2.20 GPa | 319 ksi | |
| Charpy Impact Unnotched | 6.00 J/cm2 | 28.6 ft-lb/in2 | |
| Charpy Impact, Notched | 0.300 J/cm2 | 1.43 ft-lb/in2 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.9 @Frequency 1e+6 Hz | 2.9 @Frequency 1e+6 Hz | |
| 3.2 @Frequency 100 Hz | 3.2 @Frequency 100 Hz | ||
| Dielectric Strength | 60.0 kV/mm | 1520 kV/in | |
| Dissipation Factor | 0.030 @Frequency 1e+6 Hz | 0.030 @Frequency 1e+6 Hz | |
| 0.040 @Frequency 100 Hz | 0.040 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 100 μm/m-°C @Temperature 20.0 °C | 55.6 μin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C | 181 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | |
| Vicat Softening Point | 90.0 °C | 194 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| Oxygen Index | 18 % | 18 % | |