- 密度 [g/cm3]: 1.19
- 彎曲模量 [MPa]: 3.00
- 熱變形溫度 [℃]: 94.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in3 | ISO 1183 |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 230 °C | 10 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | <= 75.0 MPa | <= 10900 psi | ISO/R527 |
| Elongation at Yield | 10 % | 10 % | ISO/R527 |
| Flexural Strength | <= 140 MPa | <= 20300 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa @Temperature 23.0 °C | 435 ksi @Temperature 73.4 °F | ISO 178 |
| Charpy Impact, Notched | 0.350 J/cm2 @Temperature 23.0 °C | 1.67 ft-lb/in2 @Temperature 73.4 °F | ISO 179 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 100 °C @Load 5.001 kg | 212 °F @Load 11.03 lb | 50°C/h; ISO 306 |
| 108 °C @Load 1.00 kg | 226 °F @Load 2.21 lb | 50°C/h; ISO 306 | |