- 熔體流動速率 [g/10min]: 150.0
- 密度 [g/cm3]: 0.947
- 彎曲強度 [MPa]: 1.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.947 g/cc | 0.0342 lb/in3 | Exxon Method |
| Apparent Bulk Density | 0.577 g/cc | 0.0208 lb/in3 | ASTM D1895 (B) |
| Viscosity | 660 cP @Temperature 121 °C | 660 cP @Temperature 250 °F | melt viscosity; ASTM D-3236 |
| Melt Flow | 150 g/10 min | 150 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 1.90 MPa | 276 psi | ASTM D638 |
| Elongation at Break | 680 % | 680 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 64.0 °C | 147 °F | Exxon Method |
| Vicat Softening Point | 89.0 °C | 192 °F | Softening Point, R&B; ASTM E-28 |