- 熔體流動速率 [g/10min]: 2.1
- 密度 [g/cm3]: 0.939
- 彎曲強度 [MPa]: 14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in3 | Exxon Method |
| Apparent Bulk Density | 0.529 g/cc | 0.0191 lb/in3 | ASTM D1895 (B) |
| Viscosity | 8300 cP @Temperature 121 °C | 8300 cP @Temperature 250 °F | melt viscosity; ASTM D-3236 |
| Melt Flow | 2.1 g/10 min | 2.1 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 86.0 °C | 187 °F | Exxon Method |
| Vicat Softening Point | 181 °C | 358 °F | Softening Point, R&B; ASTM E-28 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.494 | 1.494 | Exxon Method |