- 熔體流動速率 [g/10min]: 1.5
- 密度 [g/cm3]: 0.926
- 拉伸強度 [MPa]: 9.0
- 彎曲強度 [MPa]: 17.0
- 彎曲模量 [MPa]: 0.0920
- 脆化溫度 [℃]: -69.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in3 | Exxon Method |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50, Condition C; ASTM D1693 |
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 30 | 30 | ASTM D2240 |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | ASTM D638 |
| Elongation at Break | 1300 % | 1300 % | ASTM D638 |
| Flexural Modulus | 0.0920 GPa | 13.3 ksi | 1% Secant, ASTM D790 |
| Tensile Impact Strength | 3.80 kJ/m2 | 1.81 ft-lb/in2 | 23°C; ASTM D-1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 98.0 °C | 208 °F | Exxon Method |
| Brittleness Temperature | -69.0 °C | -92.2 °F | ASTM D746 |