- 熔體流動(dòng)速率 [g/10min]: 5.5
- 密度 [g/cm3]: 0.948
- 拉伸強(qiáng)度 [MPa]: 3.4
- 彎曲強(qiáng)度 [MPa]: 17.0
- 彎曲模量 [MPa]: 0.0310
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in3 | Exxon Method |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50, Condition A; ASTM D1693 |
| Melt Flow | 5.5 g/10 min | 5.5 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 81 | 81 | ASTM D2240 |
| Hardness, Shore D | 31 | 31 | ASTM D2240 |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 3.40 MPa | 493 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.0310 GPa | 4.50 ksi | 1% Secant, ASTM D790 |
| Tensile Impact Strength | 600 kJ/m2 | 286 ft-lb/in2 | 23°C; ASTM D-1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 77.0 °C | 171 °F | Exxon Method |
| Vicat Softening Point | 52.0 °C | 126 °F | 1000g; ASTM D-1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |