- 熔體流動速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.933
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in3 | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 4.00 MPa | 580 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 3.00 MPa | 435 psi | ASTM D882 |
| Film Elongation at Break, MD | 190 % | 190 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Secant Modulus, MD | 0.0700 GPa | 10.2 ksi | ASTM D882 |
| Secant Modulus, TD | 0.0800 GPa | 11.6 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 60 g | 60 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 50 g | 50 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 1.89 g/micron | 48.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 1.57 g/micron | 40.0 g/mil | ASTM D1922 |
| Dart Drop | 9.45 g/micron | 240 g/mil | F50; ASTM D1709 |
| Dart drop Test | 300 g | 0.662 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 29.0 MPa | 4210 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 24.0 MPa | 3480 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 87.0 °C | 189 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 3.0 % | 3.0 % | ASTM D1003 |
| Gloss | 80 % | 80 % | 45°, ASTM D-2457 |