- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.927
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in3 | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 225 % | 225 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Secant Modulus, MD | 0.250 GPa | 36.3 ksi | ASTM D882 |
| Secant Modulus, TD | 0.330 GPa | 47.9 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 600 g | 600 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 150 g | 150 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 18.9 g/micron | 480 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.72 g/micron | 120 g/mil | ASTM D1922 |
| Dart Drop | 2.52 g/micron | 64.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 80.0 g | 0.176 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 3.7 % | 3.7 % | ASTM D1003 |
| Gloss | 77 % | 77 % | 45°, ASTM D-2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |