- 熔體流動速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in3 | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.90 MPa | 1290 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.60 MPa | 1100 psi | ASTM D882 |
| Film Elongation at Break, MD | 100 % | 100 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Secant Modulus, MD | 0.140 GPa | 20.3 ksi | ASTM D882 |
| Secant Modulus, TD | 0.170 GPa | 24.7 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 400 g | 400 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 100 g | 100 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 12.6 g/micron | 320 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 3.15 g/micron | 80.0 g/mil | ASTM D1922 |
| Dart Drop | 3.15 g/micron | 80.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 100 g | 0.221 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 103 °C | 217 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | ASTM D1003 |
| Gloss | 50 % | 50 % | 45°, ASTM D-2457 |