- 熔體流動速率 [g/10min]: 800.0
- 密度 [g/cm3]: 0.953
- 彎曲模量 [MPa]: 0.0200
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in3 | ExxonMobil Method | ||
| Viscosity | 9300 cP @Temperature 190 °C | 9300 cP @Temperature 374 °F | ASTM D3236 | ||
| Vinyl Acetate Content | 27.6 % | 27.6 % | ExxonMobil Method | ||
| Melt Flow | 800 g/10 min | 800 g/10 min | 190°C, 2.16 kg; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 69 | 69 | 15s; ASTM D2240 | ||
| Hardness, Shore D | 18 | 18 | 15s; ASTM D2240 | ||
| Tensile Strength at Break | 1.93 MPa | 280 psi | ASTM D638 | ||
| Elongation at Break | 360 % | 360 % | ASTM D638 | ||
| Flexural Modulus | 0.0200 GPa | 2.90 ksi | 1% secant; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 71.1 °C | 160 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||