- 熔體流動速率 [g/10min]: 43.0
- 密度 [g/cm3]: 0.955
- 彎曲模量 [MPa]: 0.0124
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in3 | ExxonMobil Method |
| Vinyl Acetate Content | 31.4 % | 31.4 % | ExxonMobil Method |
| Melt Flow | 43 g/10 min | 43 g/10 min | 190°C, 2.16 kg; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 55 | 55 | 15s; ASTM D2240 |
| Tensile Strength at Break | 3.03 MPa | 440 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.0124 GPa | 1.80 ksi | 1% secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 57.8 °C | 136 °F | Peak Melting Temperature; ExxonMobil Method |