- 吸水率 [%]: 0.18
- 缺口沖擊強度: 0.587
- 彎曲強度 [MPa]: 62.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Water Absorption | 0.18 % @Thickness 0.508 mm | 0.18 % @Thickness 0.0200 in | 24 hr. Immersion; ASTM D570 |
| Water Absorption at Saturation | 0.70 % @Thickness 0.508 mm | 0.70 % @Thickness 0.0200 in | Long-Term Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 6.21 GPa | 900 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Izod Impact, Notched | 0.587 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.10 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistivity per Square | 1.00e+10 - 1.00e+14 ohm | 1.00e+10 - 1.00e+14 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.1 °C | 205 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 221 - 243 °C | 430 - 470 °F | Molding |
| Mold Temperature | 26.7 - 54.4 °C | 80.0 - 130 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour | |