- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 0.14
- 缺口沖擊強(qiáng)度: 0.32
- 斷裂伸長(zhǎng)率 [%]: 34.0
- 彎曲強(qiáng)度 [MPa]: 34.0
- 彎曲模量 [MPa]: 3.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in3 | ASTM D792 |
| Water Absorption | 0.14 % | 0.14 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm | 0.0040 - 0.0060 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ASTM D638 |
| Flexural Yield Strength | 34.0 MPa | 4930 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 - 0.480 J/cm @Thickness 6.35 mm | 0.599 - 0.899 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1000 - 1.00e+6 ohm-cm | 1000 - 1.00e+6 ohm-cm | ASTM D257 |
| Surface Resistance | 1000 - 1.00e+6 ohm | 1000 - 1.00e+6 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 221 - 249 °C | 430 - 480 °F | Stock |
| Mold Temperature | 82.0 - 93.0 °C | 180 - 199 °F | |
| Drying Temperature | 82.0 - 93.0 °C | 180 - 199 °F | |