- 缺口沖擊強(qiáng)度: 0.278
- 彎曲強(qiáng)度 [MPa]: 64.8
- 彎曲模量 [MPa]: 10.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 64.8 MPa | 9400 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Elongation at Break | 0.60 % | 0.60 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Tensile Modulus | 13.02 GPa | 1888 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Flexural Strength | 100 MPa | 14500 psi | ASTM D790 | ||
| Flexural Modulus | 10.3 GPa | 1500 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.278 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 0.520 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Flammability, UL94 | V-0 | V-0 | All Colors; 0.125 in. | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | Molding | ||
| Mold Temperature | 82.2 - 93.3 °C | 180 - 200 °F | |||
| Drying Temperature | 93.3 °C | 200 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Descriptive Properties | |||||
| Product Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.