- 吸水率 [%]: 0.15
- 缺口沖擊強度: 0.427
- 拉伸強度 [MPa]: 27.6
- 彎曲模量 [MPa]: 2.76
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.095 g/cc | 1.095 g/cc | Calculated |
| Water Absorption | 0.15 % @Thickness 3.17 mm | 0.15 % @Thickness 0.125 in | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.76 GPa | 400 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 44.8 MPa | 6500 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 0.800 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.00e+12 ohm | 1.00e+12 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | Annealed, 0.125 in bars; ASTM D648 |