Ultramid? 8262G HS BK-102|PA6-(MD+GF)20|BASF

Product TextsUltramid? 8262G HS BK-102 is a heat stabilized, pigmented black, 20% glass and mineral reinforced Polyamid 6 injection molding compound resulting in a balance of engineering properties with excellent dimensional stability, low warp and good resistance to sink mark formation.

機(jī)械性能(機(jī)械性能(Mechanical properties))	dry / cond	單位(Unit)	測(cè)試標(biāo)準(zhǔn)(Test Standard)
ISO數(shù)據(jù)(ISO數(shù)據(jù)(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	5200 / -	MPa	ISO 527-1/-2
破壞時(shí)應(yīng)變(Stress at break)	100 / -	MPa	ISO 527-1/-2
破壞時(shí)應(yīng)變(Strain at break)	3 / -	%	ISO 527-1/-2
簡(jiǎn)支梁缺口沖擊強(qiáng)度(Charpy notched impact strength) (+23°C)	3 / -	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	dry / cond	單位(Unit)	測(cè)試標(biāo)準(zhǔn)(Test Standard)
ISO數(shù)據(jù)(ISO數(shù)據(jù)(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
溫度負(fù)荷變形(Temp. of deflection under load) (1.80 MPa)	163 / *	°C	ISO 75-1/-2
溫度負(fù)荷變形(Temp. of deflection under load) (0.45 MPa)	211 / *	°C	ISO 75-1/-2
燃燒性(球壓痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度測(cè)試(Thickness tested)	3.0 / *	mm	IEC 60695-11-10
UL 識(shí)別(recognition)	UL / *	-	-

其他屬性(Other properties)	dry / cond	單位(Unit)	測(cè)試標(biāo)準(zhǔn)(Test Standard)
ISO數(shù)據(jù)(ISO數(shù)據(jù)(CAMPUS/ISO) Data)
吸水率(Water absorption)	7.9 / *	%	Sim. to ISO 62
吸濕性(Humidity absorption)	2.2 / *	%	Sim. to ISO 62
密度(Density)	1290 / *	kg/m3	ISO 1183

Test specimen production	值(Value)	單位(Unit)	測(cè)試標(biāo)準(zhǔn)(Test Standard)
ISO數(shù)據(jù)(ISO數(shù)據(jù)(CAMPUS/ISO) Data)
Injection Molding, melt temperature	275	°C	ISO 294
Injection Molding, mold temperature	95	°C	ISO 10724

CharacteristicsProcessingInjection MoldingDelivery formPelletsSpecial CharacteristicsHeat stabilized or stable to heatRegional AvailabilityNorth AmericaOther text informationInjection moldingPREPROCESSING Water content: 0.12% If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level. Alternatively, please contact your BASF representative. Packing pressure affects the final part and can be use It should be applied and maintained until the gate area is completely frozen off.A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Surface appearance is directly affected by injection rateDisclaimerCopyright M-Base .

轉(zhuǎn)載請(qǐng)注明: 轉(zhuǎn)自中國(guó)塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/wuxingbiao/show-94816.html

免責(zé)聲明: 本文 Ultramid? 8262G HS BK-102|PA6-(MD+GF)20|BASF 僅代表作者個(gè)人觀點(diǎn)，中國(guó)塑膠原料之家無(wú)關(guān)。中國(guó)塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問(wèn)題需要處理，請(qǐng)與我們聯(lián)絡(luò)