Product TextsUltramid? 8333G HI is glass reinforced, impact modified Polyamid 6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness and excellent moldability/surface aesthetics. It is also available in heat stabilized (Ultramid? 8333G HI HS) and/or pigmented versions.

機械性能(機械性能(Mechanical properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	9300 / 4610	MPa	ISO 527-1/-2
破壞時應變(Stress at break)	145 / 90	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	3.5 / 6	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	78 / -	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	20 / -	kJ/m2	ISO 179/1eA
簡支梁缺口沖擊強度(Charpy notched impact strength) (-30°C)	10 / -	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔化溫度(熔化溫度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	205 / *	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	220 / *	°C	ISO 75-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	24 / *	E-6/K	ISO 11359-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (normal)	84 / *	E-6/K	ISO 11359-1/-2
燃燒性(球壓痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度測試(Thickness tested)	0.8 / *	mm	IEC 60695-11-10
UL 識別(recognition)	UL / *	-	-

電氣性能(Electrical properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
相對介電常數(Relative permittivity) (100Hz)	3.6 / -	-	IEC 60250
相對介電常數(Relative permittivity) (1MHz)	3.4 / -	-	IEC 60250
耗散因數(耗散因數(Dissipation factor)) (100Hz)	0.01 / -	E-4	IEC 60250
耗散因數(耗散因數(Dissipation factor)) (1MHz)	0.01 / -	E-4	IEC 60250
體積電阻率(Volume resistivity)	>1E13 / -	Ohm*m	IEC 60093
相比漏電起痕指數(Comparative tracking index)	- / 600	-	IEC 60112

其他屬性(Other properties)	dry / cond	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
吸水率(Water absorption)	7 / *	%	Sim. to ISO 62
吸濕性(Humidity absorption)	1.8 / *	%	Sim. to ISO 62
密度(Density)	1190 / *	kg/m3	ISO 1183

流變計算屬性(Rheological calculation properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
密度(Density) of melt	1160	kg/m3	-
熔體熱導率(Thermal conductivity of melt)	0.2	W/(m K)	-
規格的熱容融化(Spec. heat capacity of melt)	1960	J/(kg K)	-

Test specimen production	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
Injection Molding, melt temperature	275	°C	ISO 294
Injection Molding, mold temperature	95	°C	ISO 10724

Diagrams Water content: 0.12% If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level. Alternatively, please contact your BASF representative. Packing pressure affects the final part and can be use It should be applied and maintained until the gate area is completely frozen off.A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Surface appearance is directly affected by injection rateDisclaimerCopyright M-Base .

Ultramid? 8333G HI|PA6-GF33|BASF