| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | |||
| 1.32 g/cc | 0.0477 lb/in³ | DAM; ISO 1183 | |||
| Water Absorption | 1.8 % @Thickness 2.00 mm |
1.8 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Moisture Absorption | 0.700 % @Thickness 2.00 mm |
0.700 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Viscosity | 29770 cP @Shear Rate 5000 1/s, Temperature 300 °C |
29770 cP @Shear Rate 5000 1/s, Temperature 572 °F |
ISO 11403-1 -2 | ||
| 35755 cP @Shear Rate 5000 1/s, Temperature 290 °C |
35755 cP @Shear Rate 5000 1/s, Temperature 554 °F |
ISO 11403-1 -2 | |||
| 43576 cP @Shear Rate 5000 1/s, Temperature 280 °C |
43576 cP @Shear Rate 5000 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |||
| 69238 cP @Shear Rate 500 1/s, Temperature 300 °C |
69238 cP @Shear Rate 500 1/s, Temperature 572 °F |
ISO 11403-1 -2 | |||
| 83186 cP @Shear Rate 500 1/s, Temperature 290 °C |
83186 cP @Shear Rate 500 1/s, Temperature 554 °F |
ISO 11403-1 -2 | |||
| 101400 cP @Shear Rate 500 1/s, Temperature 280 °C |
101400 cP @Shear Rate 500 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | DAM; ISO 294-4 2577 | ||
| 0.0030 cm/cm @Thickness 3.20 mm |
0.0030 in/in @Thickness 0.126 in |
DAM | |||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | DAM; ISO 294-4 2577 | ||
| 0.010 cm/cm @Thickness 3.20 mm |
0.010 in/in @Thickness 0.126 in |
DAM; ASTM D149 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 170 MPa | 24700 psi | DAM; ISO 527-1/-2 | ||
| Elongation at Break | 2.5 % | 2.5 % | DAM; ISO 527-1/-2 | ||
| Tensile Modulus | 9.80 GPa | 1420 ksi | DAM; ISO 527-1/-2 | ||
| Flexural Modulus | 8.40 GPa | 1220 ksi | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | DAM; ISO 180/1A | ||
| 10.0 kJ/m² @Temperature -40.0 °C |
4.76 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A | |||
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | DAM; ISO 179/1eA | ||
| 1.00 J/cm² @Temperature -40.0 °C |
4.76 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V | 600 V | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C | 8.33 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| Specific Heat Capacity | 2.13 J/g-°C | 0.509 BTU/lb-°F | |||
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | of melt | ||
| Melting Point | 218 °C | 424 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | ||
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
DAM; IEC 60695-11-10 | |||
| De |
|||||
| Additives | Lubricants | ||||
| Release agent | |||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PA612-GF33< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA612-GF33 | ||||
| PA612-GF33 | ISO 1043 | ||||
| Special characteristics | Heat stabilised or stable to heat | ||||
| UL recognition | UL | DAM | |||
概述
PA塑料(尼龍，聚酰胺)，英文名稱:Polyamide
PA的品種繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近幾年開發(fā)的半芳香族尼龍PA6T和特種尼龍等很多新品種。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收縮率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型溫度：220-300℃
干燥條件：100-110℃/12小時(shí)
堅(jiān)韌、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃燒鑒別方法：火焰上端黃色，下端藍(lán)色，燃燒后塑料熔滴落，起泡，離火后特殊的羊毛，指甲燒焦味和帶芹菜味
|
尼龍6： |
彈性好，沖擊強(qiáng)度，吸水較大 |
|
尼龍66： |
性能優(yōu)于尼龍6，強(qiáng)度高，耐磨性好 |
|
尼龍610： |
與尼龍66相似，但吸水小，剛度低 |
|
尼龍1010： |
半透明，吸水小。耐寒性較好。適于制作一般機(jī)械零件、減磨耐磨零件、傳動(dòng)零件以及化工、電器、儀表等零件 |
成型性能
1、結(jié)晶料，熔點(diǎn)較高，熔融溫度范圍窄，熱穩(wěn)定性差，料溫超過300度、滯留時(shí)間超過30分鐘即分解。較易吸濕，需干燥，含水量不得超過0.3%。
2、流動(dòng)性好，易溢料。宜用自鎖時(shí)噴嘴，并應(yīng)加熱。
3、成型收縮范圍及收縮率大，方向性明顯，易發(fā)生縮孔、變形等。
4、模溫按塑件壁厚在20～90度范圍內(nèi)選取，注射壓力按注射機(jī)類型、料溫、塑件形狀尺寸、模具澆注系統(tǒng)選定，成型周期按塑件壁厚選定。樹脂粘度小時(shí)，注射、冷卻時(shí)間應(yīng)取長，并用白油作脫模劑。
5、模具澆注系統(tǒng)的形式和尺寸，增大流道和澆口尺寸可減少縮水。
聚酰胺的不足之處在于：由于熱膨脹和吸水性所至的尺寸精度不夠，耐酸性差，硬度和彈性模量不夠。經(jīng)改良以后，也是比較優(yōu)秀的工程塑料之一。
應(yīng)用
汽車制造方面
用于制造燃料濾網(wǎng)、燃料過濾器、罐、捕集器、儲(chǔ)油槽、發(fā)動(dòng)機(jī)汽缸蓋罩、散熱器水缸、平衡旋轉(zhuǎn)軸齒輪。也可用在汽車的電器配件、接線柱等。另外，它還可用作驅(qū)動(dòng)、控制部件等。
電器電子工業(yè)
可用于制造電飯鍋、電動(dòng)吸塵器、高頻電子食品加熱器，電器產(chǎn)品的接線柱、開關(guān)和電阻器等。
醫(yī)療器械儀器
用于醫(yī)用輸血管、取血器、輸液器等。PA單絲可做外科手術(shù)縫線、假發(fā)等；另外，電子打字機(jī)的數(shù)字旋轉(zhuǎn)盤、接線柱、傳動(dòng)齒輪、印刷機(jī)的帶式過濾片等。
其它方面
用于制作一次性打火機(jī)體、堿性干電池襯墊，摩托車駕駛員的頭盔，辦公機(jī)器外殼，辦公用椅的角輪、座和靠背，冰鞋、釣魚線等，PA薄膜氣體阻隔性能優(yōu)良，而且耐油性、耐低溫沖擊性、耐穿透性好，可用于肉、火腿腸等冷凍食品的包裝。聚酰胺還可棒材和板材，也作齒輪或其它傳動(dòng)裝置。
上海浩銘塑膠有限公司！本公司承諾，所有產(chǎn)品都是原廠家，原包裝一線獨(dú)家營銷！
可提供以下報(bào)告：COA（產(chǎn)地證明）SGS（檢測報(bào)告）MSDS（成分報(bào)告）FDA（食品安全報(bào)告）UL黃卡（出口報(bào)告）正規(guī)發(fā)票！歡迎新老客戶來電咨詢：
聯(lián)系人：鄧小姐
聯(lián)系電話：13917657923
聯(lián)系QQ:996152797
聯(lián)系郵箱：996152797@qq.com