| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | |||
| 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 | |||
| Water Absorption | 8.5 % @Thickness 2.00 mm |
8.5 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Moisture Absorption | 2.60 % @Thickness 2.00 mm |
2.60 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Viscosity | 92024 cP @Shear Rate 5000 1/s, Temperature 300 °C |
92024 cP @Shear Rate 5000 1/s, Temperature 572 °F |
ISO 11403-1 -2 | ||
| 104500 cP @Shear Rate 5000 1/s, Temperature 290 °C |
104500 cP @Shear Rate 5000 1/s, Temperature 554 °F |
ISO 11403-1 -2 | |||
| 119500 cP @Shear Rate 5000 1/s, Temperature 280 °C |
119500 cP @Shear Rate 5000 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |||
| 358900 cP @Shear Rate 500 1/s, Temperature 300 °C |
358900 cP @Shear Rate 500 1/s, Temperature 572 °F |
ISO 11403-1 -2 | |||
| 447000 cP @Shear Rate 500 1/s, Temperature 290 °C |
447000 cP @Shear Rate 500 1/s, Temperature 554 °F |
ISO 11403-1 -2 | |||
| 551300 cP @Shear Rate 500 1/s, Temperature 280 °C |
551300 cP @Shear Rate 500 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |||
| Viscosity Test | 330 cm³/g | 330 cm³/g | DAM; ISO 307 1157 1628 | ||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | DAM; ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | DAM; ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 6.00 MPa @Strain 1.60 %, Temperature 150 °C |
870 psi @Strain 1.60 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | ||
| 8.60 MPa @Strain 2.40 %, Temperature 150 °C |
1250 psi @Strain 2.40 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 10.2 MPa @Strain 3.00 %, Temperature 150 °C |
1480 psi @Strain 3.00 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 16.1 MPa @Strain 6.00 %, Temperature 150 °C |
2340 psi @Strain 6.00 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 19.5 MPa @Strain 0.600 %, Temperature 23.0 °C |
2830 psi @Strain 0.600 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 36.9 MPa @Strain 1.10 %, Temperature -40.0 °C |
5350 psi @Strain 1.10 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 72.1 MPa @Strain 2.60 %, Temperature 23.0 °C |
10500 psi @Strain 2.60 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 76.8 MPa @Strain 2.90 %, Temperature 23.0 °C |
11100 psi @Strain 2.90 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 80.8 MPa @Strain 3.20 %, Temperature 23.0 °C |
11700 psi @Strain 3.20 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 88.7 MPa @Strain 2.90 %, Temperature -40.0 °C |
12900 psi @Strain 2.90 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 110 MPa @Strain 4.10 %, Temperature -40.0 °C |
16000 psi @Strain 4.10 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 124.9 MPa @Strain 6.00 %, Temperature -40.0 °C |
18120 psi @Strain 6.00 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50%RH; ISO 527-1/-2 | ||
| 84.0 MPa | 12200 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 35 % | 35 % | DAM; Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 4.3 % | 4.3 % | DAM; ISO 527-1/-2 | ||
| 29 % | 29 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 1.20 GPa | 174 ksi | 50%RH; ISO 527-1/-2 | ||
| 3.10 GPa | 450 ksi | DAM; ISO 527-1/-2 | |||
| Flexural Modulus | 2.80 GPa | 406 ksi | DAM; ISO 178 | ||
| Secant Modulus | 0.178 GPa @Strain 19.0 %, Temperature 100 °C |
25.8 ksi @Strain 19.0 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | ||
| 0.301 GPa @Strain 8.50 %, Temperature 100 °C |
43.7 ksi @Strain 8.50 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 0.402 GPa @Strain 4.10 %, Temperature 100 °C |
58.4 ksi @Strain 4.10 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 0.471 GPa @Strain 2.10 %, Temperature 100 °C |
68.4 ksi @Strain 2.10 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 0.536 GPa @Strain 1.10 %, Temperature 100 °C |
77.8 ksi @Strain 1.10 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 2.44 GPa @Strain 3.40 %, Temperature 23.0 °C |
354 ksi @Strain 3.40 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 2.55 GPa @Strain 4.50 %, Temperature -40.0 °C |
370 ksi @Strain 4.50 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 2.60 GPa @Strain 3.00 %, Temperature 23.0 °C |
378 ksi @Strain 3.00 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 2.77 GPa @Strain 2.60 %, Temperature 23.0 °C |
402 ksi @Strain 2.60 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 3.06 GPa @Strain 2.90 %, Temperature -40.0 °C |
444 ksi @Strain 2.90 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 3.25 GPa @Strain 0.600 %, Temperature 23.0 °C |
471 ksi @Strain 0.600 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 3.35 GPa @Strain 1.10 %, Temperature -40.0 °C |
487 ksi @Strain 1.10 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | DAM; ISO 180/1A | ||
| Charpy Impact Unnotched | NB | NB | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | DAM; ISO 179/1eA | ||
| 2.10 J/cm² | 9.99 ft-lb/in² | 50%RH; ISO 179/1eA | |||
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |||
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | 50%RH; IEC 60093 | ||
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | DAM; IEC 60093 | |||
| Comparative Tracking Index | 600 V | 600 V | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 2.79 J/g-°C | 0.667 BTU/lb-°F | |||
| Thermal Conductivity | 0.160 W/m-K | 1.11 BTU-in/hr-ft²-°F | of melt | ||
| Melting Point | 262 °C | 504 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | ||
| Vicat Softening Point | 221 °C | 430 °F | DAM; 50°C/h 50N; ISO 306 | ||
| Oxygen Index | 20 % | 20 % | DAM; ISO 4589-1/-2 | ||
| De |
|||||
| Additives | Release agent | ||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PA66< | ISO 11469 | |||
| Processing | Casting | ||||
| Coatable | |||||
| Film Extrusion | |||||
| Injection Moulding | |||||
| Other Extrusion | |||||
| Profile Extrusion | |||||
| Sheet Extrusion | |||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA66 | ||||
| Special characteristics | Heat stabilised or stable to heat | ||||
概述
PA塑料(尼龍，聚酰胺)，英文名稱:Polyamide
PA的品種繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近幾年開發的半芳香族尼龍PA6T和特種尼龍等很多新品種。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收縮率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型溫度：220-300℃
干燥條件：100-110℃/12小時
堅韌、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃燒鑒別方法：火焰上端黃色，下端藍色，燃燒后塑料熔滴落，起泡，離火后特殊的羊毛，指甲燒焦味和帶芹菜味
|
尼龍6： |
彈性好，沖擊強度，吸水較大 |
|
尼龍66： |
性能優于尼龍6，強度高，耐磨性好 |
|
尼龍610： |
與尼龍66相似，但吸水小，剛度低 |
|
尼龍1010： |
半透明，吸水小。耐寒性較好。適于制作一般機械零件、減磨耐磨零件、傳動零件以及化工、電器、儀表等零件 |
成型性能
1、結晶料，熔點較高，熔融溫度范圍窄，熱穩定性差，料溫超過300度、滯留時間超過30分鐘即分解。較易吸濕，需干燥，含水量不得超過0.3%。
2、流動性好，易溢料。宜用自鎖時噴嘴，并應加熱。
3、成型收縮范圍及收縮率大，方向性明顯，易發生縮孔、變形等。
4、模溫按塑件壁厚在20～90度范圍內選取，注射壓力按注射機類型、料溫、塑件形狀尺寸、模具澆注系統選定，成型周期按塑件壁厚選定。樹脂粘度小時，注射、冷卻時間應取長，并用白油作脫模劑。
5、模具澆注系統的形式和尺寸，增大流道和澆口尺寸可減少縮水。
聚酰胺的不足之處在于：由于熱膨脹和吸水性所至的尺寸精度不夠，耐酸性差，硬度和彈性模量不夠。經改良以后，也是比較優秀的工程塑料之一。
應用
汽車制造方面
用于制造燃料濾網、燃料過濾器、罐、捕集器、儲油槽、發動機汽缸蓋罩、散熱器水缸、平衡旋轉軸齒輪。也可用在汽車的電器配件、接線柱等。另外，它還可用作驅動、控制部件等。
電器電子工業
可用于制造電飯鍋、電動吸塵器、高頻電子食品加熱器，電器產品的接線柱、開關和電阻器等。
醫療器械儀器
用于醫用輸血管、取血器、輸液器等。PA單絲可做外科手術縫線、假發等；另外，電子打字機的數字旋轉盤、接線柱、傳動齒輪、印刷機的帶式過濾片等。
其它方面
用于制作一次性打火機體、堿性干電池襯墊，摩托車駕駛員的頭盔，辦公機器外殼，辦公用椅的角輪、座和靠背，冰鞋、釣魚線等，PA薄膜氣體阻隔性能優良，而且耐油性、耐低溫沖擊性、耐穿透性好，可用于肉、火腿腸等冷凍食品的包裝。聚酰胺還可棒材和板材，也作齒輪或其它傳動裝置。