| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption at Saturation | 0.91 % | 0.91 % | DAM; Immersion 24h; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | DAM; ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | DAM; ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 112 MPa | 16200 psi | 50%RH; ISO 527-1/-2 | ||
| 148 MPa | 21500 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 3.6 % | 3.6 % | DAM; ISO 527-1/-2 | ||
| 6.6 % | 6.6 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 6.50 GPa | 943 ksi | 50%RH; ISO 527-1/-2 | ||
| 8.80 GPa | 1280 ksi | DAM; ISO 527-1/-2 | |||
| Flexural Strength | 214 MPa | 31000 psi | DAM; ISO 178 | ||
| Flexural Modulus | 7.60 GPa | 1100 ksi | DAM; ISO 178 | ||
| Shear Modulus | 0.521 GPa @Temperature 150 °C |
75.6 ksi @Temperature 302 °F |
DAM; Dynamic; ISO 11403-1 -2 | ||
| 0.6072 GPa @Temperature 110 °C |
88.07 ksi @Temperature 230 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 1.1235 GPa @Temperature 60.0 °C |
162.95 ksi @Temperature 140 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 1.5884 GPa @Temperature 10.0 °C |
230.38 ksi @Temperature 50.0 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 1.6393 GPa @Temperature -20.0 °C |
237.76 ksi @Temperature -4.00 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 1.941 GPa @Temperature -50.0 °C |
281.5 ksi @Temperature -58.0 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 21.0 kJ/m² | 9.99 ft-lb/in² | DAM; ISO 180/1A | ||
| 26.0 kJ/m² | 12.4 ft-lb/in² | 50%RH; ISO 180/1A | |||
| 15.0 kJ/m² @Temperature -40.0 °C |
7.14 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A | |||
| 16.0 kJ/m² @Temperature -30.0 °C |
7.61 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 180/1A | |||
| 17.0 kJ/m² @Temperature -30.0 °C |
8.09 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 180/1A | |||
| Charpy Impact Unnotched | 9.60 J/cm² | 45.7 ft-lb/in² | 50%RH; ISO 179/1eU | ||
| 9.70 J/cm² | 46.2 ft-lb/in² | DAM; ISO 179/1eU | |||
| 9.70 J/cm² @Temperature -40.0 °C |
46.2 ft-lb/in² @Temperature -40.0 °F |
50%RH; ISO 179/1eU | |||
| 10.9 J/cm² @Temperature -40.0 °C |
51.9 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | DAM; ISO 179/1eA | ||
| 2.70 J/cm² | 12.8 ft-lb/in² | 50%RH; ISO 179/1eA | |||
| 1.70 J/cm² @Temperature -30.0 °C |
8.09 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |||
| 1.80 J/cm² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA | |||
| 1.80 J/cm² @Temperature -40.0 °C |
8.57 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 400 V | 400 V | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C | 8.33 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 119 µm/m-°C | 66.1 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| Melting Point | 262 °C | 504 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 261 °C | 502 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | DAM; ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
DAM; IEC 60695-11-10 | ||
| De |
|||||
| Emission of organic compounds | 25.3 µgC/g | VDA 277 | |||
| Odour | class 3 | VDA 270 | |||
| Part Marking Code | >PA66-IGF33< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA66-IGF33 | ||||
| Special characteristics | Heat stabilised or stable to heat | ||||
概述
PA塑料(尼龍，聚酰胺)，英文名稱:Polyamide
PA的品種繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近幾年開發的半芳香族尼龍PA6T和特種尼龍等很多新品種。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收縮率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型溫度：220-300℃
干燥條件：100-110℃/12小時
堅韌、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃燒鑒別方法：火焰上端黃色，下端藍色，燃燒后塑料熔滴落，起泡，離火后特殊的羊毛，指甲燒焦味和帶芹菜味
|
尼龍6： |
彈性好，沖擊強度，吸水較大 |
|
尼龍66： |
性能優于尼龍6，強度高，耐磨性好 |
|
尼龍610： |
與尼龍66相似，但吸水小，剛度低 |
|
尼龍1010： |
半透明，吸水小。耐寒性較好。適于制作一般機械零件、減磨耐磨零件、傳動零件以及化工、電器、儀表等零件 |
成型性能
1、結晶料，熔點較高，熔融溫度范圍窄，熱穩定性差，料溫超過300度、滯留時間超過30分鐘即分解。較易吸濕，需干燥，含水量不得超過0.3%。
2、流動性好，易溢料。宜用自鎖時噴嘴，并應加熱。
3、成型收縮范圍及收縮率大，方向性明顯，易發生縮孔、變形等。
4、模溫按塑件壁厚在20～90度范圍內選取，注射壓力按注射機類型、料溫、塑件形狀尺寸、模具澆注系統選定，成型周期按塑件壁厚選定。樹脂粘度小時，注射、冷卻時間應取長，并用白油作脫模劑。
5、模具澆注系統的形式和尺寸，增大流道和澆口尺寸可減少縮水。
聚酰胺的不足之處在于：由于熱膨脹和吸水性所至的尺寸精度不夠，耐酸性差，硬度和彈性模量不夠。經改良以后，也是比較優秀的工程塑料之一。
應用
汽車制造方面
用于制造燃料濾網、燃料過濾器、罐、捕集器、儲油槽、發動機汽缸蓋罩、散熱器水缸、平衡旋轉軸齒輪。也可用在汽車的電器配件、接線柱等。另外，它還可用作驅動、控制部件等。
電器電子工業
可用于制造電飯鍋、電動吸塵器、高頻電子食品加熱器，電器產品的接線柱、開關和電阻器等。
醫療器械儀器
用于醫用輸血管、取血器、輸液器等。PA單絲可做外科手術縫線、假發等；另外，電子打字機的數字旋轉盤、接線柱、傳動齒輪、印刷機的帶式過濾片等。
其它方面
用于制作一次性打火機體、堿性干電池襯墊，摩托車駕駛員的頭盔，辦公機器外殼，辦公用椅的角輪、座和靠背，冰鞋、釣魚線等，PA薄膜氣體阻隔性能優良，而且耐油性、耐低溫沖擊性、耐穿透性好，可用于肉、火腿腸等冷凍食品的包裝。聚酰胺還可棒材和板材，也作齒輪或其它傳動裝置。