- 缺口沖擊強度: 1.17
- 拉伸強度 [MPa]: 181.0
- 彎曲模量 [MPa]: 11.0
- 熱變形溫度 [℃]: 299.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | Method A; ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 181 MPa | 26300 psi | ASTM D638 |
| Tensile Strength, Yield | 181 MPa | 26300 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 13.0 GPa | 1890 ksi | ASTM D638 |
| Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm @Thickness 3.18 mm | 2.19 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 9.13 J/cm @Thickness 3.18 mm | 17.1 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 11.2 kJ/m2 | 5.33 ft-lb/in2 | ISO 180 |
| Izod Impact, Unnotched (ISO) | 58.9 kJ/m2 | 28.0 ft-lb/in2 | ISO 180 |
| Falling Dart Impact | 8.10 J | 5.97 ft-lb | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 μm/m-°C @Temperature 20.0 °C | 11.1 μin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| CTE, linear, Transverse to Flow | 36.0 μm/m-°C @Temperature 20.0 °C | 20.0 μin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 299 °C | 570 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 299 °C | 570 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 379 - 388 °C | 714 - 730 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.10 % | 0.10 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |