- 缺口沖擊強度: 0.883
- 彎曲強度 [MPa]: 245.0
- 彎曲模量 [MPa]: 17.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 245 MPa | 35600 psi | |||
| Flexural Strength | 343.35 MPa | 49799 psi | |||
| Flexural Modulus | 17.7 GPa | 2560 ksi | |||
| Izod Impact, Notched | 0.883 J/cm | 1.65 ft-lb/in | |||
| Coefficient of Friction, Dynamic | 0.166 @Time 3600 sec, Pressure 1.96 MPa | 0.166 @Time 1.00 hour, Pressure 284 psi | 0.2 m/s | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 100000 ohm-cm | 100000 ohm-cm | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 390 °C | 734 °F | |||
| Descriptive Properties | |||||
| Abrasion Weight (g) | 0.0015 | Wear Tester 0.2m/s; 20kgf/cm2; 1hr | |||
| Coefficient of Abrasion (10-3 cm2-sec/kgf-m-hr) | 0.1358 | Wear Tester 0.2m/s; 20kgf/cm2; 1hr | |||