- 熔體流動速率 [g/10min]: 36.0
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.53
- 彎曲模量 [MPa]: 3.80
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 | ||
| Water Absorption | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.017 cm/cm | 0.017 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ASTM D955 | ||
| Melt Flow | 36 g/10 min @Load 2.16 kg, Temperature 400 °C | 36 g/10 min @Load 4.76 lb, Temperature 752 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 100 MPa | 14500 psi | ASTM D638 | ||
| Elongation at Break | 10 - 20 % | 10 - 20 % | ASTM D638 | ||
| Elongation at Yield | 5.2 % | 5.2 % | ASTM D638 | ||
| Tensile Modulus | 3.70 GPa | 537 ksi | ASTM D638 | ||
| Flexural Strength | 153 MPa | 22200 psi | ASTM D790 | ||
| Flexural Modulus | 3.80 GPa | 551 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 | ||
| NB | NB | ASTM D256 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 50.0 μm/m-°C @Temperature -50.0 - 50.0 °C | 27.8 μin/in-°F @Temperature -58.0 - 122 °F | TMA; ASTM E831 | ||
| Melting Point | 343 °C | 649 °F | Peak; ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 | ||
| Glass Transition Temp, Tg | 147 °C | 297 °F | ASTM D3418 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 355 °C | 671 °F | |||
| Middle Barrel Temperature | 365 °C | 689 °F | |||
| Front Barrel Temperature | 370 °C | 698 °F | |||
| Nozzle Temperature | 375 °C | 707 °F | |||
| Mold Temperature | 175 - 205 °C | 347 - 401 °F | |||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | ||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Ductile | ||||
| Fatigue Resistant | |||||
| Flame Retardant | |||||
| Good Chemical Resistance | |||||
| Good Dimensional Stability | |||||
| Good Impact Resistance | |||||
| High Flow | |||||
| High Heat Resistance | |||||
| Forms | Pellets | non-lubricated | |||
| Generic | PEEK | ||||
| Injection Rate | Fast | ||||
| Processing Method | Injection Molding | ||||
| Machining | |||||
| Profile Extrusion | |||||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 | ||||
| Uses | Aircraft Applications | ||||
| Connectors | |||||
| Electrical/Electronic Applications | |||||
| Film | |||||
| Industrial Applications | |||||
| Medical/Healthcare Applications | |||||
| Oil/Gas Applications | |||||
| Pump Parts | |||||
| Seals | |||||