- 熔體流動速率 [g/10min]: 2.0
- 吸水率 [%]: 0.03
- 缺口沖擊強度: 0.69
- 拉伸強度 [MPa]: 197.0
- 彎曲模量 [MPa]: 16.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 | ||
| Water Absorption | 0.030 % @Time 86400 sec | 0.030 % @Time 24.0 hour | ASTM D570 | ||
| Viscosity | 380000 cP @Shear Rate 1000 1/s, Temperature 400 °C | 380000 cP @Shear Rate 1000 1/s, Temperature 752 °F | Melt; ASTM D3835 | ||
| Linear Mold Shrinkage, Flow | 0.00 - 0.0020 cm/cm @Thickness 3.18 mm | 0.00 - 0.0020 in/in @Thickness 0.125 in | 5" x 0.5" x 0.125" bars; ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.013 - 0.015 cm/cm @Thickness 3.18 mm | 0.013 - 0.015 in/in @Thickness 0.125 in | 5" x 0.5" x 0.125" bars; ASTM D955 | ||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 400 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 752 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 90 | 90 | M-Scale; ASTM D785 | ||
| Tensile Strength | 161 MPa | 23400 psi | ASTM D638 | ||
| Tensile Strength, Yield | 197 MPa | 28600 psi | ISO 527-2/1A/5 | ||
| Elongation at Break | 1.5 % | 1.5 % | 5.0 mm/min; ASTM D638 | ||
| 1.5 % | 1.5 % | ISO 527-2/1A/5 | |||
| Tensile Modulus | 18.3 GPa | 2650 ksi | ASTM D638 | ||
| 25.3 GPa | 3670 ksi | ISO 527-2/1A/1 | |||
| Flexural Strength | 265 MPa | 38400 psi | ASTM D790 | ||
| 273 MPa | 39600 psi | ISO 178 | |||
| Flexural Modulus | 16.6 GPa | 2410 ksi | ASTM D790 | ||
| 24.1 GPa | 3500 ksi | ISO 178 | |||
| Compressive Strength | 127 MPa | 18400 psi | ASTM D695 | ||
| Shear Strength | 84.1 MPa | 12200 psi | ASTM D732 | ||
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 | ||
| 5.30 J/cm | 9.93 ft-lb/in | ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 8.50 kJ/m2 | 4.04 ft-lb/in2 | ISO 180 | ||
| Izod Impact, Unnotched (ISO) | 43.0 kJ/m2 | 20.5 ft-lb/in2 | ISO 180 | ||
| Coefficient of Friction, Dynamic | 0.070 | 0.070 | Lubricated conditions: 800 fpm and 750 psi; ASTM D3702 | ||
| 0.12 | 0.12 | Lubricated conditions: 75 fpm and 1000 psi; ASTM D1894 | |||
| 0.34 | 0.34 | Dry conditions: 800 fpm and 31.25 psi; ASTM D1894 | |||
| 0.45 | 0.45 | Dry conditions: 200 fpm and 125 psi; ASTM D3702 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 17.0 μm/m-°C @Temperature -50.0 - 50.0 °C | 9.44 μin/in-°F @Temperature -58.0 - 122 °F | TMA; ASTM E831 | ||
| Specific Heat Capacity | 1.25 J/g-°C @Temperature 50.0 °C | 0.299 BTU/lb-°F @Temperature 122 °F | DSC | ||
| 1.67 J/g-°C @Temperature 200 °C | 0.399 BTU/lb-°F @Temperature 392 °F | DSC | |||
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft2-°F | ASTM E1530 | ||
| Melting Point | 342 °C | 648 °F | Peak; ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 299 °C | 570 °F | Annealed; ASTM D648 | ||
| Glass Transition Temp, Tg | 152 °C | 306 °F | ASTM D3418 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 366 °C | 691 °F | |||
| Middle Barrel Temperature | 371 °C | 700 °F | |||
| Front Barrel Temperature | 377 °C | 711 °F | |||
| Nozzle Temperature | 382 °C | 720 °F | |||
| Mold Temperature | 177 - 204 °C | 351 - 399 °F | |||
| Drying Temperature | 149 °C | 300 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Descriptive Properties | |||||
| Additive | Carbon Fiber + PTFE Lubricant | ||||
| Appearance | Black | ||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Fatigue Resistant | ||||
| Flame Retardant | |||||
| Good Chemical Resistance | |||||
| Good Dimensional Stability | |||||
| Good Wear Resistance | |||||
| High Heat Resistance | |||||
| Forms | Pellets | ||||
| Generic | PEEK | ||||
| Injection Rate | Fast | ||||
| Processing Method | Injection Molding | ||||
| Machining | |||||
| Profile Extrusion | |||||
| RoHS Compliance | RoHS Compliant | ||||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 | ||||
| Uses | Automotive Applications | ||||
| Bushings | |||||
| Gears | |||||
| Oil/Gas Applications | |||||
| Thrust Washer | |||||