- 密度 [g/cm3]: 1.36
- 缺口沖擊強度: 0.48
- 拉伸強度 [MPa]: 149.0
- 彎曲模量 [MPa]: 10.27
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in3 | ASTM D792 |
| 1.36 g/cc | 0.0491 lb/in3 | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec | 0.0030 in/in @Time 24.0 hour | ASTM D955 |
| 0.0034 cm/cm @Time 86400 sec | 0.0034 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Time 86400 sec | 0.0060 in/in @Time 24.0 hour | ASTM D955 |
| 0.0062 cm/cm @Time 86400 sec | 0.0062 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 149 MPa | 21600 psi | ISO 527 |
| 149 MPa | 21600 psi | ASTM D638 | |
| Tensile Strength, Yield | 149 MPa | 21600 psi | ISO 527 |
| 149 MPa | 21600 psi | ASTM D638 | |
| Elongation at Break | 2.1 % | 2.1 % | ISO 527 |
| 2.3 % | 2.3 % | ASTM D638 | |
| Elongation at Yield | 2.1 % | 2.1 % | ISO 527 |
| 2.3 % | 2.3 % | ASTM D638 | |
| Tensile Modulus | 11.5 GPa | 1670 ksi | 1 mm/min; ISO 527 |
| 11.99 GPa | 1739 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 241 MPa | 35000 psi | ISO 178 |
| 241 MPa | 35000 psi | ASTM D790 | |
| Flexural Modulus | 10.27 GPa | 1490 ksi | ISO 178 |
| 10.79 GPa | 1565 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.76 J/cm | 10.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m2 | 6.19 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 212 kJ/m2 | 101 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J | 1.48 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+6 - 1.00e+8 ohm-cm | 1.00e+6 - 1.00e+8 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+6 - 1.00e+8 ohm | 1.00e+6 - 1.00e+8 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 39.6 μm/m-°C @Temperature -40.0 - 40.0 °C | 22.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 41.2 μm/m-°C @Temperature -40.0 - 40.0 °C | 22.9 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 16.2 μm/m-°C @Temperature -40.0 - 40.0 °C | 9.00 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 16.3 μm/m-°C @Temperature -40.0 - 40.0 °C | 9.06 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 300 °C @Thickness 3.20 mm | 572 °F @Thickness 0.126 in | unannealed; ASTM D648 | |