- 密度 [g/cm3]: 1.43
- 缺口沖擊強度: 0.58
- 拉伸強度 [MPa]: 161.0
- 彎曲模量 [MPa]: 10.3
- 熱變形溫度 [℃]: 335.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Density | 1.43 g/cc | 0.0517 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec | 0.0040 - 0.0060 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec | 0.0070 - 0.0090 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 159 MPa | 23100 psi | Type I, 5 mm/min; ASTM D638 |
| 160 MPa | 23200 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 161 MPa | 23400 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 |
| 2.1 % | 2.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 11.87 GPa | 1722 ksi | 1 mm/min; ISO 527 |
| 12.36 GPa | 1793 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 229 MPa | 33200 psi | ISO 178 |
| 239 MPa | 34700 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 10.3 GPa | 1490 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 10.32 GPa | 1497 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.83 J/cm | 9.05 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m2 | 14.3 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C | 5.16 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.34 | 0.34 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.42 | 0.42 | ASTM D3702 Modified |
| K (wear) Factor | 4.03 x 10-8 mm3/N-M | 2.00 x 10-10 in3-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 32.2 x 10-8 mm3/N-M | 16.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 18.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 10.0 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 42.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 23.3 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 335 °C | 635 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 336 °C @Thickness 3.20 mm | 637 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 335 °C | 635 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 322 °C @Thickness 3.20 mm | 612 °F @Thickness 0.126 in | unannealed; ASTM D648 | |