- 密度 [g/cm3]: 1.38
- 缺口沖擊強度: 0.85
- 拉伸強度 [MPa]: 77.0
- 彎曲模量 [MPa]: 2.89
- 熱變形溫度 [℃]: 158.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Density | 1.38 g/cc | 0.0499 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm @Time 86400 sec | 0.0070 - 0.010 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 |
| 76.0 MPa | 11000 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 77.0 MPa | 11200 psi | 5 mm/min; ISO 527 |
| 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 12.8 % | 12.8 % | 5 mm/min; ISO 527 |
| 35 % | 35 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 6.1 % | 6.1 % | 5 mm/min; ISO 527 |
| 6.4 % | 6.4 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.16 GPa | 458 ksi | 1 mm/min; ISO 527 |
| 3.36 GPa | 487 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 104 MPa | 15100 psi | ISO 178 |
| Flexural Modulus | 2.89 GPa | 419 ksi | 2 mm/min; ISO 178 |
| 3.22 GPa | 467 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 18.5 J/cm | 34.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 101 kJ/m2 | 48.1 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C | 3.69 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.47 | 0.47 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 42.3 x 10-8 mm3/N-M | 21.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 54.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 30.0 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 59.7 μm/m-°C @Temperature -30.0 - 30.0 °C | 33.2 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 153 °C @Thickness 3.20 mm | 307 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 147 °C @Thickness 3.20 mm | 297 °F @Thickness 0.126 in | unannealed; ASTM D648 | |