- 熔體流動速率 [g/10min]: 17.0
- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 0.04
- 缺口沖擊強度: 0.235
- 拉伸強度 [MPa]: 64.0
- 斷裂伸長率 [%]: 48.3
- 彎曲強度 [MPa]: 2.7
- 彎曲模量 [MPa]: 2.41
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 - 1.63 g/cc | 0.0477 - 0.0589 lb/in3 | Average value: 1.42 g/cc Grade Count:50 |
| Filler Content | 5.00 - 45.0 % | 5.00 - 45.0 % | Average value: 22.7 % Grade Count:15 |
| Water Absorption | 0.0400 - 0.200 % | 0.0400 - 0.200 % | Average value: 0.0979 % Grade Count:29 |
| Viscosity | 260000 - 340000 cP @Temperature 400 - 400 °C | 260000 - 340000 cP @Temperature 752 - 752 °F | Average value: 300000 cP Grade Count:2 |
| Linear Mold Shrinkage | 0.00100 - 0.0250 cm/cm | 0.00100 - 0.0250 in/in | Average value: 0.0115 cm/cm Grade Count:35 |
| Linear Mold Shrinkage, Transverse | 0.00600 - 0.0190 cm/cm | 0.00600 - 0.0190 in/in | Average value: 0.0129 cm/cm Grade Count:4 |
| Melt Flow | 17.0 - 50.0 g/10 min | 17.0 - 50.0 g/10 min | Average value: 27.7 g/10 min Grade Count:10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90.0 - 117 | 90.0 - 117 | Average value: 98.6 Grade Count:7 |
| Hardness, Shore D | 85.0 - 90.0 | 85.0 - 90.0 | Average value: 87.7 Grade Count:9 |
| Tensile Strength, Ultimate | 2.70 - 180 MPa | 392 - 26100 psi | Average value: 77.7 MPa Grade Count:48 |
| Tensile Strength, Yield | 64.0 - 155 MPa | 9280 - 22500 psi | Average value: 100 MPa Grade Count:6 |
| Elongation at Break | 0.900 - 25.0 % | 0.900 - 25.0 % | Average value: 7.44 % Grade Count:31 |
| Elongation at Yield | 1.50 - 8.50 % | 1.50 - 8.50 % | Average value: 5.35 % Grade Count:20 |
| Modulus of Elasticity | 1.17 - 15.0 GPa | 170 - 2180 ksi | Average value: 4.01 GPa Grade Count:44 |
| Flexural Yield Strength | 48.3 - 270 MPa | 7000 - 39200 psi | Average value: 125 MPa Grade Count:49 |
| Flexural Modulus | 2.41 - 14.5 GPa | 350 - 2100 ksi | Average value: 4.14 GPa Grade Count:48 |
| Compressive Yield Strength | 35.0 - 221 MPa | 5080 - 32000 psi | Average value: 107 MPa Grade Count:9 |
| 65.0 - 65.0 MPa @Temperature 120 - 120 °C | 9430 - 9430 psi @Temperature 248 - 248 °F | Average value: 65.0 MPa Grade Count:1 | |
| Compressive Modulus | 2.28 - 5.45 GPa | 330 - 791 ksi | Average value: 3.21 GPa Grade Count:5 |
| Izod Impact, Notched | 0.235 - 1.07 J/cm | 0.440 - 2.00 ft-lb/in | Average value: 0.646 J/cm Grade Count:23 |
| Izod Impact, Unnotched | 3.20 - 5340 J/cm | 6.00 - 10000 ft-lb/in | Average value: 10.5 J/cm Grade Count:13 |
| Izod Impact, Notched (ISO) | 0.750 - 8.80 kJ/m2 | 0.357 - 4.19 ft-lb/in2 | Average value: 4.85 kJ/m2 Grade Count:3 |
| Charpy Impact Unnotched | 2.30 - 1000 J/cm2 | 10.9 - 4760 ft-lb/in2 | Average value: 5.62 J/cm2 Grade Count:16 |
| 4.50 - 6.00 J/cm2 @Temperature -30.0 - -30.0 °C | 21.4 - 28.6 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 5.25 J/cm2 Grade Count:2 | |
| Charpy Impact, Notched | 0.400 - 1.20 J/cm2 | 1.90 - 5.71 ft-lb/in2 | Average value: 0.692 J/cm2 Grade Count:13 |
| 0.500 - 0.500 J/cm2 @Temperature -30.0 - -30.0 °C | 2.38 - 2.38 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 0.500 J/cm2 Grade Count:1 | |
| Coefficient of Friction | 0.0400 - 0.520 | 0.0400 - 0.520 | Average value: 0.174 Grade Count:12 |
| 0.0800 - 0.0900 @Temperature 100 - 100 °C | 0.0800 - 0.0900 @Temperature 212 - 212 °F | Average value: 0.0850 Grade Count:2 | |
| Coefficient of Friction, Static | 0.120 - 0.430 | 0.120 - 0.430 | Average value: 0.184 Grade Count:11 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 30000 - 6.00e+16 ohm-cm | 30000 - 6.00e+16 ohm-cm | Average value: 9.54e+15 ohm-cm Grade Count:10 |
| Surface Resistance | 10000 - 1.00e+14 ohm | 10000 - 1.00e+14 ohm | Average value: 1.68e+13 ohm Grade Count:7 |
| Insulation Resistance | 1.00e+9 - 1.00e+12 ohm | 1.00e+9 - 1.00e+12 ohm | Average value: 9.29e+11 ohm Grade Count:14 |
| Dielectric Constant | 2.80 - 3.50 | 2.80 - 3.50 | Average value: 3.27 Grade Count:5 |
| Dielectric Strength | 0.100 - 27.0 kV/mm | 2.54 - 686 kV/in | Average value: 18.2 kV/mm Grade Count:7 |
| Dissipation Factor | 0.00200 - 0.0610 | 0.00200 - 0.0610 | Average value: 0.0200 Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 9.00 - 65.0 μm/m-°C | 5.00 - 36.1 μin/in-°F | Average value: 44.3 μm/m-°C Grade Count:10 |
| 9.00 - 140 μm/m-°C @Temperature >=143 °C | 5.00 - 77.8 μin/in-°F @Temperature >=289 °F | Average value: 94.8 μm/m-°C Grade Count:2 | |
| Specific Heat Capacity | 1.05 - 1.80 J/g-°C | 0.251 - 0.430 BTU/lb-°F | Average value: 1.30 J/g-°C Grade Count:3 |
| Thermal Conductivity | 0.240 - 0.250 W/m-K | 1.67 - 1.74 BTU-in/hr-ft2-°F | Average value: 0.246 W/m-K Grade Count:5 |
| Melting Point | 340 - 343 °C | 644 - 649 °F | Average value: 342 °C Grade Count:16 |
| Maximum Service Temperature, Air | 115 - 260 °C | 239 - 500 °F | Average value: 249 °C Grade Count:20 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 - 290 °C | 300 - 554 °F | Average value: 182 °C Grade Count:16 |
| Vicat Softening Point | 280 - 290 °C | 536 - 554 °F | Average value: 281 °C Grade Count:7 |
| Glass Transition Temp, Tg | 143 - 146 °C | 289 - 295 °F | Average value: 144 °C Grade Count:5 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:28 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 343 - 390 °C | 650 - 734 °F | Average value: 387 °C Grade Count:19 |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | Average value: 370 °C Grade Count:17 |
| Melt Temperature | 349 - 400 °C | 660 - 752 °F | Average value: 380 °C Grade Count:31 |
| Mold Temperature | 135 - 218 °C | 275 - 425 °F | Average value: 184 °C Grade Count:35 |
| Drying Temperature | 120 - 170 °C | 248 - 338 °F | Average value: 138 °C Grade Count:32 |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Average value: 3.13 hour Grade Count:8 |
| <= 3.00 hour @Temperature 149 - 149 °C | <= 3.00 hour @Temperature 300 - 300 °F | Average value: 3.00 hour Grade Count:1 | |
| Moisture Content | 0.100 % | 0.100 % | Average value: 0.100 % Grade Count:11 |
| Dew Point | -28.9 °C | -20.0 °F | Average value: -28.9 °C Grade Count:10 |
| Injection Pressure | 49.6 - 124 MPa | 7200 - 18000 psi | Average value: 100 MPa Grade Count:13 |