- 熔體流動速率 [g/10min]: 1.1
- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.03
- 缺口沖擊強度: 0.235
- 拉伸強度 [MPa]: 86.2
- 斷裂伸長率 [%]: 48.3
- 彎曲強度 [MPa]: 51.7
- 彎曲模量 [MPa]: 2.80
- 硬度: 118.0
- 熱變形溫度 [℃]: 288.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 - 1.75 g/cc | 0.0470 - 0.0632 lb/in3 | Average value: 1.43 g/cc Grade Count:181 |
| Filler Content | 10.0 - 60.0 % | 10.0 - 60.0 % | Average value: 28.2 % Grade Count:52 |
| Water Absorption | 0.0300 - 0.180 % | 0.0300 - 0.180 % | Average value: 0.100 % Grade Count:114 |
| Moisture Absorption at Equilibrium | 0.0600 - 0.160 % | 0.0600 - 0.160 % | Average value: 0.127 % Grade Count:3 |
| Water Absorption at Saturation | 0.0600 - 0.400 % | 0.0600 - 0.400 % | Average value: 0.276 % Grade Count:10 |
| Additive Loading | 10.0 - 30.0 % | 10.0 - 30.0 % | Average value: 22.0 % Grade Count:5 |
| Viscosity | 200000 - 850000 cP @Temperature 400 - 400 °C | 200000 - 850000 cP @Temperature 752 - 752 °F | Average value: 464000 cP Grade Count:6 |
| 270000 - 920000 cP @Temperature 400 - 400 °C | 270000 - 920000 cP @Temperature 752 - 752 °F | Average value: 464000 cP Grade Count:4 | |
| 270000 - 920000 cP @Shear Rate 1000 - 1000 1/s | 270000 - 920000 cP @Shear Rate 1000 - 1000 1/s | Average value: 464000 cP Grade Count:4 | |
| Linear Mold Shrinkage | 0.000 - 0.0160 cm/cm | 0.000 - 0.0160 in/in | Average value: 0.00248 cm/cm Grade Count:140 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00100 - 0.00300 cm/cm | 0.00100 - 0.00300 in/in | Average value: 0.00145 cm/cm Grade Count:10 |
| Linear Mold Shrinkage, Transverse | 0.00300 - 0.0170 cm/cm | 0.00300 - 0.0170 in/in | Average value: 0.00829 cm/cm Grade Count:21 |
| Melt Flow | 1.10 - 122 g/10 min | 1.10 - 122 g/10 min | Average value: 30.2 g/10 min Grade Count:30 |
| Spiral Flow | 4.20 - 130 cm | 1.65 - 51.2 in | Average value: 54.3 cm Grade Count:6 |
| Crystallinity | 17.0 - 35.0 % | 17.0 - 35.0 % | Average value: 27.0 % Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 80.0 - 125 | 80.0 - 125 | Average value: 102 Grade Count:26 |
| Hardness, Rockwell R | 118 - 124 | 118 - 124 | Average value: 120 Grade Count:5 |
| Hardness, Shore D | 85.0 - 93.0 | 85.0 - 93.0 | Average value: 89.6 Grade Count:24 |
| Ball Indentation Hardness | 215 - 440 MPa | 31200 - 63800 psi | Average value: 323 MPa Grade Count:4 |
| Tensile Strength, Ultimate | 51.7 - 2070 MPa | 7500 - 300000 psi | Average value: 202 MPa Grade Count:168 |
| 65.0 - 180 MPa @Temperature 125 - 275 °C | 9430 - 26100 psi @Temperature 257 - 527 °F | Average value: 110 MPa Grade Count:1 | |
| Tensile Strength, Yield | 86.2 - 2070 MPa | 12500 - 300000 psi | Average value: 372 MPa Grade Count:21 |
| Elongation at Break | 0.300 - 7.00 % | 0.300 - 7.00 % | Average value: 1.90 % Grade Count:99 |
| Elongation at Yield | 0.500 - 6.80 % | 0.500 - 6.80 % | Average value: 2.28 % Grade Count:77 |
| Modulus of Elasticity | 1.00 - 138 GPa | 145 - 20000 ksi | Average value: 21.5 GPa Grade Count:165 |
| Flexural Yield Strength | 48.3 - 2000 MPa | 7000 - 290000 psi | Average value: 297 MPa Grade Count:171 |
| 60.0 - 250 MPa @Temperature 125 - 225 °C | 8700 - 36300 psi @Temperature 257 - 437 °F | Average value: 139 MPa Grade Count:2 | |
| Flexural Modulus | 2.80 - 124 GPa | 406 - 18000 ksi | Average value: 18.1 GPa Grade Count:174 |
| 6.55002 - 6.55002 GPa @Temperature 149 - 149 °C | 950.015 - 950.015 ksi @Temperature 300 - 300 °F | Average value: 6.55 GPa Grade Count:1 | |
| Compressive Yield Strength | 4.14 - 1360 MPa | 600 - 197000 psi | Average value: 262 MPa Grade Count:32 |
| 70.0 - 200 MPa @Temperature 120 - 200 °C | 10200 - 29000 psi @Temperature 248 - 392 °F | Average value: 135 MPa Grade Count:1 | |
| Compressive Modulus | 2.28 - 124 GPa | 330 - 18000 ksi | Average value: 29.6 GPa Grade Count:14 |
| Poissons Ratio | 0.300 - 0.440 | 0.300 - 0.440 | Average value: 0.400 Grade Count:4 |
| Shear Modulus | 4.51 - 8.03 GPa | 654 - 1160 ksi | Average value: 5.54 GPa Grade Count:4 |
| Shear Strength | 68.9 - 186 MPa | 10000 - 27000 psi | Average value: 96.1 MPa Grade Count:12 |
| 23.4422 - 68.2581 MPa @Temperature 65.6 - 260 °C | 3400.01 - 9900.02 psi @Temperature 150 - 500 °F | Average value: 47.3 MPa Grade Count:1 | |
| Izod Impact, Notched | 0.235 - 7.50 J/cm | 0.440 - 14.1 ft-lb/in | Average value: 0.933 J/cm Grade Count:83 |
| Izod Impact, Unnotched | 2.67 - 9.08 J/cm | 5.00 - 17.0 ft-lb/in | Average value: 5.98 J/cm Grade Count:55 |
| Izod Impact, Notched (ISO) | 0.600 - 10.0 kJ/m2 | 0.286 - 4.76 ft-lb/in2 | Average value: 6.43 kJ/m2 Grade Count:16 |
| Izod Impact, Unnotched (ISO) | 3.50 - 55.0 kJ/m2 | 1.67 - 26.2 ft-lb/in2 | Average value: 34.6 kJ/m2 Grade Count:16 |
| Charpy Impact Unnotched | 0.800 - 12.0 J/cm2 | 3.81 - 57.1 ft-lb/in2 | Average value: 4.00 J/cm2 Grade Count:75 |
| 2.00 - 3.00 J/cm2 @Temperature -30.0 - -30.0 °C | 9.52 - 14.3 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 2.41 J/cm2 Grade Count:8 | |
| Charpy Impact, Notched | 0.300 - 1.00 J/cm2 | 1.43 - 4.76 ft-lb/in2 | Average value: 0.694 J/cm2 Grade Count:36 |
| 0.700 - 1.00 J/cm2 @Temperature -30.0 - -30.0 °C | 3.33 - 4.76 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 0.786 J/cm2 Grade Count:7 | |
| Falling Dart Impact | 4.40 - 12.5 J | 3.25 - 9.22 ft-lb | Average value: 7.66 J Grade Count:5 |
| Coefficient of Friction | 0.0700 - 0.450 | 0.0700 - 0.450 | Average value: 0.198 Grade Count:29 |
| Coefficient of Friction, Static | 0.110 - 0.320 | 0.110 - 0.320 | Average value: 0.171 Grade Count:15 |
| K (wear) Factor | 26.2 - 302 x 10-8 mm3/N-M | 13.0 - 150 x 10-10 in3-min/ft-lb-hr | Average value: 174 x 10-8 mm3/N-M Grade Count:5 |
| Limiting Pressure Velocity | 0.420 - 1.23 MPa-m/sec | 12000 - 35000 psi-ft/min | Average value: 0.812 MPa-m/sec Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.100 - 1.00e+7 ohm-cm | 0.100 - 1.00e+7 ohm-cm | Average value: 454000 ohm-cm Grade Count:44 |
| Surface Resistance | 100 - 1.00e+12 ohm | 100 - 1.00e+12 ohm | Average value: 1.32e+10 ohm Grade Count:77 |
| Insulation Resistance | 100 - 1.00e+12 ohm | 100 - 1.00e+12 ohm | Average value: 2.23e+10 ohm Grade Count:70 |
| Dielectric Strength | 1.26 - 24.5 kV/mm | 32.0 - 622 kV/in | Average value: 9.01 kV/mm Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 5.00 - 48.6 μm/m-°C | 2.78 - 27.0 μin/in-°F | Average value: 19.0 μm/m-°C Grade Count:42 |
| 5.00 - 110 μm/m-°C @Temperature 22.8 - 250 °C | 2.78 - 61.1 μin/in-°F @Temperature 73.0 - 482 °F | Average value: 37.6 μm/m-°C Grade Count:8 | |
| Specific Heat Capacity | 1.80 - 1.85 J/g-°C | 0.430 - 0.442 BTU/lb-°F | Average value: 1.82 J/g-°C Grade Count:6 |
| 1.13 - 1.84 J/g-°C @Temperature 50.0 - 200 °C | 0.270 - 0.440 BTU/lb-°F @Temperature 122 - 392 °F | Average value: 1.50 J/g-°C Grade Count:4 | |
| Thermal Conductivity | 0.240 - 22.0 W/m-K | 1.67 - 153 BTU-in/hr-ft2-°F | Average value: 1.51 W/m-K Grade Count:31 |
| Melting Point | 334 - 344 °C | 633 - 651 °F | Average value: 342 °C Grade Count:35 |
| Maximum Service Temperature, Air | 249 - 315 °C | 480 - 599 °F | Average value: 264 °C Grade Count:84 |
| Deflection Temperature at 0.46 MPa (66 psi) | 288 - 300 °C | 550 - 572 °F | Average value: 293 °C Grade Count:7 |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 - 349 °C | 302 - 660 °F | Average value: 284 °C Grade Count:108 |
| Vicat Softening Point | 295 - 325 °C | 563 - 617 °F | Average value: 312 °C Grade Count:25 |
| Heat Distortion Temperature | 235 - 253 °C | 455 - 487 °F | Average value: 241 °C Grade Count:4 |
| Minimum Service Temperature, Air | -80.0 - -20.0 °C | -112 - -4.00 °F | Average value: -55.0 °C Grade Count:4 |
| Glass Transition Temp, Tg | 143 - 152 °C | 289 - 306 °F | Average value: 146 °C Grade Count:13 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:98 |
| Oxygen Index | 40.0 - 43.0 % | 40.0 - 43.0 % | Average value: 41.0 % Grade Count:3 |
| Glow Wire Test | 960 °C | 1760 °F | Average value: 960 °C Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 343 - 390 °C | 650 - 734 °F | Average value: 385 °C Grade Count:93 |
| Nozzle Temperature | 360 - 390 °C | 680 - 734 °F | Average value: 371 °C Grade Count:76 |
| Melt Temperature | 349 - 400 °C | 660 - 752 °F | Average value: 381 °C Grade Count:116 |
| Mold Temperature | 135 - 218 °C | 275 - 425 °F | Average value: 186 °C Grade Count:140 |
| Drying Temperature | 120 - 170 °C | 248 - 338 °F | Average value: 138 °C Grade Count:120 |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Average value: 3.29 hour Grade Count:35 |
| Moisture Content | 0.0100 - 0.100 % | 0.0100 - 0.100 % | Average value: 0.0918 % Grade Count:33 |
| Dew Point | -28.9 °C | -20.0 °F | Average value: -28.9 °C Grade Count:27 |
| Injection Pressure | 82.7 - 124 MPa | 12000 - 18000 psi | Average value: 103 MPa Grade Count:47 |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | Average value: 0.517 MPa Grade Count:6 |