- 熔體流動速率 [g/10min]: 0.7
- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.011
- 缺口沖擊強度: 0.112
- 拉伸強度 [MPa]: 97.0
- 斷裂伸長率 [%]: 67.6
- 彎曲強度 [MPa]: 51.0
- 彎曲模量 [MPa]: 4.00
- 硬度: 115.0
- 熱變形溫度 [℃]: 299.0
- 脆化溫度 [℃]: -65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 - 1.84 g/cc | 0.0470 - 0.0665 lb/in3 | Average value: 1.53 g/cc Grade Count:151 |
| Filler Content | 5.00 - 60.0 % | 5.00 - 60.0 % | Average value: 26.4 % Grade Count:57 |
| Water Absorption | 0.0110 - 0.500 % | 0.0110 - 0.500 % | Average value: 0.110 % Grade Count:93 |
| Moisture Absorption at Equilibrium | 0.160 - 0.500 % | 0.160 - 0.500 % | Average value: 0.340 % Grade Count:4 |
| Water Absorption at Saturation | 0.300 - 0.500 % | 0.300 - 0.500 % | Average value: 0.388 % Grade Count:13 |
| Additive Loading | 15.0 - 40.0 % | 15.0 - 40.0 % | Average value: 26.0 % Grade Count:5 |
| Viscosity | 210000 - 560000 cP @Temperature 400 - 400 °C | 210000 - 560000 cP @Temperature 752 - 752 °F | Average value: 458000 cP Grade Count:8 |
| 350000 - 850000 cP @Temperature 400 - 400 °C | 350000 - 850000 cP @Temperature 752 - 752 °F | Average value: 458000 cP Grade Count:3 | |
| 350000 - 850000 cP @Shear Rate 1000 - 1000 1/s | 350000 - 850000 cP @Shear Rate 1000 - 1000 1/s | Average value: 458000 cP Grade Count:3 | |
| Linear Mold Shrinkage | 0.00100 - 0.0150 cm/cm | 0.00100 - 0.0150 in/in | Average value: 0.00434 cm/cm Grade Count:125 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00200 - 0.00600 cm/cm | 0.00200 - 0.00600 in/in | Average value: 0.00411 cm/cm Grade Count:9 |
| Linear Mold Shrinkage, Transverse | 0.00450 - 0.0160 cm/cm | 0.00450 - 0.0160 in/in | Average value: 0.00945 cm/cm Grade Count:22 |
| Melt Flow | 0.700 - 110 g/10 min | 0.700 - 110 g/10 min | Average value: 30.1 g/10 min Grade Count:18 |
| Spiral Flow | 5.60 - 4100 cm | 2.20 - 1610 in | Average value: 431 cm Grade Count:11 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85.0 - 108 | 85.0 - 108 | Average value: 102 Grade Count:21 |
| Hardness, Rockwell R | 115 - 126 | 115 - 126 | Average value: 123 Grade Count:11 |
| Hardness, Shore D | 86.0 - 93.0 | 86.0 - 93.0 | Average value: 89.9 Grade Count:17 |
| Tensile Strength, Ultimate | 51.0 - 260 MPa | 7400 - 37700 psi | Average value: 143 MPa Grade Count:141 |
| 35.0 - 140 MPa @Temperature 125 - 275 °C | 5080 - 20300 psi @Temperature 257 - 527 °F | Average value: 76.0 MPa Grade Count:4 | |
| Tensile Strength, Yield | 97.0 - 220 MPa | 14100 - 31900 psi | Average value: 163 MPa Grade Count:15 |
| Elongation at Break | 1.00 - 10.0 % | 1.00 - 10.0 % | Average value: 2.77 % Grade Count:89 |
| Elongation at Yield | 1.00 - 5.00 % | 1.00 - 5.00 % | Average value: 2.67 % Grade Count:57 |
| Modulus of Elasticity | 3.86 - 25.5 GPa | 561 - 3700 ksi | Average value: 10.5 GPa Grade Count:133 |
| Flexural Yield Strength | 67.6 - 350 MPa | 9800 - 50800 psi | Average value: 215 MPa Grade Count:141 |
| 50.0 - 190 MPa @Temperature 125 - 275 °C | 7250 - 27600 psi @Temperature 257 - 527 °F | Average value: 107 MPa Grade Count:2 | |
| Flexural Modulus | 4.00 - 24.1 GPa | 580 - 3500 ksi | Average value: 9.49 GPa Grade Count:145 |
| Compressive Yield Strength | 4.14 - 250 MPa | 600 - 36300 psi | Average value: 172 MPa Grade Count:17 |
| 55.0 - 160 MPa @Temperature 120 - 250 °C | 7980 - 23200 psi @Temperature 248 - 482 °F | Average value: 106 MPa Grade Count:4 | |
| Compressive Modulus | 3.45 - 4.14 GPa | 500 - 600 ksi | Average value: 3.79 GPa Grade Count:6 |
| Poissons Ratio | 0.340 - 0.450 | 0.340 - 0.450 | Average value: 0.413 Grade Count:3 |
| Shear Modulus | 2.40 - 4.25 GPa | 348 - 616 ksi | Average value: 3.28 GPa Grade Count:3 |
| Shear Strength | 75.8 - 105 MPa | 11000 - 15300 psi | Average value: 92.4 MPa Grade Count:7 |
| Izod Impact, Notched | 0.112 - 10.0 J/cm | 0.210 - 18.7 ft-lb/in | Average value: 1.22 J/cm Grade Count:81 |
| Izod Impact, Unnotched | 3.74 - 13.3 J/cm | 7.00 - 25.0 ft-lb/in | Average value: 7.78 J/cm Grade Count:52 |
| Izod Impact, Notched (ISO) | 0.500 - 13.0 kJ/m2 | 0.238 - 6.19 ft-lb/in2 | Average value: 6.28 kJ/m2 Grade Count:12 |
| Izod Impact, Unnotched (ISO) | 3.00 - 62.0 kJ/m2 | 1.43 - 29.5 ft-lb/in2 | Average value: 33.1 kJ/m2 Grade Count:12 |
| Charpy Impact Unnotched | 1.80 - 6.00 J/cm2 | 8.57 - 28.6 ft-lb/in2 | Average value: 3.98 J/cm2 Grade Count:54 |
| 2.00 - 5.50 J/cm2 @Temperature -30.0 - -30.0 °C | 9.52 - 26.2 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 4.12 J/cm2 Grade Count:17 | |
| Charpy Impact, Notched | 0.300 - 1.50 J/cm2 | 1.43 - 7.14 ft-lb/in2 | Average value: 0.877 J/cm2 Grade Count:17 |
| 0.700 - 4.00 J/cm2 @Temperature -30.0 - -30.0 °C | 3.33 - 19.0 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 1.52 J/cm2 Grade Count:6 | |
| Coefficient of Friction | 0.240 - 0.450 | 0.240 - 0.450 | Average value: 0.311 Grade Count:31 |
| Coefficient of Friction, Static | 0.250 - 0.300 | 0.250 - 0.300 | Average value: 0.285 Grade Count:23 |
| K (wear) Factor | 171 - 353 x 10-8 mm3/N-M | 85.0 - 175 x 10-10 in3-min/ft-lb-hr | Average value: 243 x 10-8 mm3/N-M Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10.0 - 3.80e+17 ohm-cm | 10.0 - 3.80e+17 ohm-cm | Average value: 2.33e+16 ohm-cm Grade Count:40 |
| Surface Resistance | 1000 - 1.90e+17 ohm | 1000 - 1.90e+17 ohm | Average value: 9.56e+15 ohm Grade Count:36 |
| Insulation Resistance | 1.00e+12 - 1.00e+16 ohm | 1.00e+12 - 1.00e+16 ohm | Average value: 3.89e+14 ohm Grade Count:52 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:3 |
| Dielectric Constant | 2.80 - 4.20 | 2.80 - 4.20 | Average value: 3.33 Grade Count:19 |
| Dielectric Strength | 0.630 - 175 kV/mm | 16.0 - 4450 kV/in | Average value: 24.3 kV/mm Grade Count:23 |
| Dissipation Factor | 0.00100 - 0.0100 | 0.00100 - 0.0100 | Average value: 0.00331 Grade Count:18 |
| Comparative Tracking Index | 150 - 175 V | 150 - 175 V | Average value: 154 V Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 13.0 - 55.0 μm/m-°C | 7.22 - 30.6 μin/in-°F | Average value: 25.9 μm/m-°C Grade Count:60 |
| 15.0 - 130 μm/m-°C @Temperature 100 - 100 °C | 8.33 - 72.2 μin/in-°F @Temperature 212 - 212 °F | Average value: 60.9 μm/m-°C Grade Count:10 | |
| CTE, linear, Transverse to Flow | 36.0 - 110 μm/m-°C | 20.0 - 61.1 μin/in-°F | Average value: 59.8 μm/m-°C Grade Count:3 |
| Specific Heat Capacity | 1.70 - 2.16 J/g-°C | 0.406 - 0.516 BTU/lb-°F | Average value: 1.78 J/g-°C Grade Count:12 |
| 1.28 - 1.73 J/g-°C @Temperature 50.0 - 200 °C | 0.306 - 0.413 BTU/lb-°F @Temperature 122 - 392 °F | Average value: 1.50 J/g-°C Grade Count:2 | |
| Thermal Conductivity | 0.250 - 0.918 W/m-K | 1.74 - 6.37 BTU-in/hr-ft2-°F | Average value: 0.395 W/m-K Grade Count:46 |
| Melting Point | 340 - 374 °C | 644 - 705 °F | Average value: 343 °C Grade Count:28 |
| Maximum Service Temperature, Air | 249 - 480 °C | 480 - 896 °F | Average value: 264 °C Grade Count:68 |
| Deflection Temperature at 0.46 MPa (66 psi) | 299 - 340 °C | 570 - 644 °F | Average value: 313 °C Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 157 - 343 °C | 315 - 649 °F | Average value: 290 °C Grade Count:104 |
| Vicat Softening Point | 300 - 330 °C | 572 - 626 °F | Average value: 321 °C Grade Count:29 |
| Brittleness Temperature | -65.0 °C | -85.0 °F | Average value: -65.0 °C Grade Count:4 |
| Glass Transition Temp, Tg | 143 - 150 °C | 289 - 302 °F | Average value: 145 °C Grade Count:19 |
| UL RTI, Electrical | 240 - 260 °C | 464 - 500 °F | Average value: 247 °C Grade Count:6 |
| UL RTI, Mechanical with Impact | 180 - 240 °C | 356 - 464 °F | Average value: 213 °C Grade Count:6 |
| UL RTI, Mechanical without Impact | 220 - 240 °C | 428 - 464 °F | Average value: 237 °C Grade Count:6 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:120 |
| Oxygen Index | 35.0 - 45.0 % | 35.0 - 45.0 % | Average value: 41.4 % Grade Count:7 |
| Glow Wire Test | 960 °C | 1760 °F | Average value: 960 °C Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 100 - 416 °C | 212 - 780 °F | Average value: 380 °C Grade Count:72 |
| Nozzle Temperature | 360 - 390 °C | 680 - 734 °F | Average value: 372 °C Grade Count:58 |
| Melt Temperature | 349 - 400 °C | 660 - 752 °F | Average value: 380 °C Grade Count:102 |
| Mold Temperature | 135 - 250 °C | 275 - 482 °F | Average value: 186 °C Grade Count:126 |
| Drying Temperature | 120 - 170 °C | 248 - 338 °F | Average value: 139 °C Grade Count:108 |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Average value: 3.18 hour Grade Count:44 |
| 3.00 - 5.00 hour @Temperature 120 - 150 °C | 3.00 - 5.00 hour @Temperature 248 - 302 °F | Average value: 3.50 hour Grade Count:3 | |
| Moisture Content | 0.100 % | 0.100 % | Average value: 0.100 % Grade Count:35 |
| Dew Point | -28.9 °C | -20.0 °F | Average value: -28.9 °C Grade Count:30 |
| Injection Pressure | 49.6 - 124 MPa | 7200 - 18000 psi | Average value: 102 MPa Grade Count:49 |
| Back Pressure | 0.000 - 0.689 MPa | 0.000 - 99.9 psi | Average value: 0.419 MPa Grade Count:7 |