- 熔體流動速率 [g/10min]: 0.1
- 密度 [g/cm3]: 0.88
- 吸水率 [%]: 0.05
- 缺口沖擊強(qiáng)度: 0.641
- 拉伸強(qiáng)度 [MPa]: 0.207
- 斷裂伸長率 [%]: 2.66
- 彎曲強(qiáng)度 [MPa]: 0.345
- 彎曲模量 [MPa]: 0.00138
- 脆化溫度 [℃]: -65.0
- 透光率 [%]: 82.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.880 - 11.0 g/cc | 0.0318 - 0.397 lb/in3 | Average value: 1.06 g/cc Grade Count:909 |
| Volatiles | 0.400 - 0.750 % | 0.400 - 0.750 % | Average value: 0.574 % Grade Count:19 |
| Water Absorption | 0.0500 % | 0.0500 % | Average value: 0.0500 % Grade Count:10 |
| Viscosity | 0.0300 - 30000 cP | 0.0300 - 30000 cP | Average value: 5130 cP Grade Count:23 |
| 1600 - 2300 cP @Temperature 180 - 180 °C | 1600 - 2300 cP @Temperature 356 - 356 °F | Average value: 2080 cP Grade Count:4 | |
| Viscosity Measurement | 4.00 - 57.0 @Temperature 150 - 180 °C | 4.00 - 57.0 @Temperature 302 - 356 °F | Average value: 13.6 Grade Count:139 |
| Viscosity Measure | 6.00 - 80.0 cSt | 6.00 - 80.0 cSt | Average value: 24.9 cSt Grade Count:15 |
| Linear Mold Shrinkage | 0.00300 - 0.0470 cm/cm | 0.00300 - 0.0470 in/in | Average value: 0.0183 cm/cm Grade Count:156 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.0190 cm/cm | 0.00100 - 0.0190 in/in | Average value: 0.00861 cm/cm Grade Count:23 |
| Melt Flow | 0.100 - 57.0 g/10 min | 0.100 - 57.0 g/10 min | Average value: 8.67 g/10 min Grade Count:51 |
| Deformation | 30.0 - 64.0 % @Temperature 700 - 700 °C | 30.0 - 64.0 % @Temperature 1290 - 1290 °F | Average value: 41.4 % Grade Count:8 |
| 30.0 - 64.0 % @Time 79200 - 79200 sec | 30.0 - 64.0 % @Time 22.0 - 22.0 hour | Average value: 41.4 % Grade Count:8 | |
| Ash | 0.350 - 39.0 % | 0.350 - 39.0 % | Average value: 15.0 % Grade Count:12 |
| Chemical Properties | Metric | English | Comments |
| Styrene Content | 20.0 - 55.0 % | 20.0 - 55.0 % | Average value: 31.9 % Grade Count:19 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 6.00 - 98.0 | 6.00 - 98.0 | Average value: 59.2 Grade Count:904 |
| Hardness, Shore D | 10.0 - 73.0 | 10.0 - 73.0 | Average value: 41.4 Grade Count:48 |
| Tensile Strength, Ultimate | 0.345 - 80.0 MPa | 50.0 - 11600 psi | Average value: 7.62 MPa Grade Count:822 |
| Tensile Strength, Yield | 0.207 - 20.0 MPa | 30.0 - 2900 psi | Average value: 3.90 MPa Grade Count:119 |
| Elongation at Break | 5.50 - 1900 % | 5.50 - 1900 % | Average value: 601 % Grade Count:898 |
| Modulus of Elasticity | 0.000300 - 2.41 GPa | 0.0435 - 350 ksi | Average value: 0.0220 GPa Grade Count:203 |
| Flexural Yield Strength | 2.66 - 100 MPa | 386 - 14500 psi | Average value: 30.0 MPa Grade Count:5 |
| Flexural Modulus | 0.00138 - 2.55 GPa | 0.200 - 370 ksi | Average value: 0.649 GPa Grade Count:8 |
| Rebound | 22.0 - 65.0 % | 22.0 - 65.0 % | Average value: 46.9 % Grade Count:27 |
| Adhesive Bond Strength | 0.550 - 2.65 MPa | 79.8 - 384 psi | Average value: 1.13 MPa Grade Count:10 |
| Izod Impact, Notched | 0.641 - 5340 J/cm | 1.20 - 10000 ft-lb/in | Average value: 2.39 J/cm Grade Count:24 |
| Izod Impact, Unnotched | 1.60 - 5340 J/cm | 3.00 - 10000 ft-lb/in | Average value: 6.01 J/cm Grade Count:23 |
| Penetration | 50.0 | 50.0 | Average value: 50.0 Grade Count:4 |
| Tear Strength | 5.78 - 230 kN/m | 33.0 - 1310 pli | Average value: 29.1 kN/m Grade Count:545 |
| Peel Strength | 0.000 - 50.0 kN/m | 0.000 - 285 pli | Average value: 8.17 kN/m Grade Count:92 |
| Graves Tear Strength | 2.50 - 92.0 kN/m | 14.3 - 525 pli | Average value: 18.2 kN/m Grade Count:210 |
| Taber Abrasion, mg/1000 Cycles | 30.0 - 540 | 30.0 - 540 | Average value: 184 Grade Count:26 |
| Compression Set | 7.00 - 90.0 % | 7.00 - 90.0 % | Average value: 26.9 % Grade Count:513 |
| 16.0 - 95.0 % @Temperature 70.0 - 100 °C | 16.0 - 95.0 % @Temperature 158 - 212 °F | Average value: 56.2 % Grade Count:148 | |
| 16.0 - 99.0 % @Temperature -25.0 - 158 °C | 16.0 - 99.0 % @Temperature -13.0 - 316 °F | Average value: 56.2 % Grade Count:320 | |
| 16.0 - 99.0 % @Time 79200 - 605000 sec | 16.0 - 99.0 % @Time 22.0 - 168 hour | Average value: 56.2 % Grade Count:320 | |
| Tensile Set | 33.0 - 95.0 % @Temperature 70.0 - 70.0 °C | 33.0 - 95.0 % @Temperature 158 - 158 °F | Average value: 58.4 % Grade Count:15 |
| 33.0 - 95.0 % @Time 79200 - 79200 sec | 33.0 - 95.0 % @Time 22.0 - 22.0 hour | Average value: 58.4 % Grade Count:15 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0100 - 1.00e+16 ohm-cm | 0.0100 - 1.00e+16 ohm-cm | Average value: 2.42e+15 ohm-cm Grade Count:90 |
| Surface Resistance | 10.0 - 9.90e+12 ohm | 10.0 - 9.90e+12 ohm | Average value: 5.80e+11 ohm Grade Count:21 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:13 |
| Dielectric Constant | 2.10 - 2.80 | 2.10 - 2.80 | Average value: 2.47 Grade Count:21 |
| Dielectric Strength | 24.0 - 50.0 kV/mm | 610 - 1270 kV/in | Average value: 29.7 kV/mm Grade Count:55 |
| Dissipation Factor | 0.000100 - 0.00510 | 0.000100 - 0.00510 | Average value: 0.00248 Grade Count:21 |
| Comparative Tracking Index | 550 - 600 V | 550 - 600 V | Average value: 564 V Grade Count:21 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 50.0 - 170 °C | 122 - 338 °F | Average value: 92.3 °C Grade Count:290 |
| Minimum Service Temperature, Air | -60.0 - -30.0 °C | -76.0 - -22.0 °F | Average value: -46.4 °C Grade Count:309 |
| Brittleness Temperature | -65.0 - -21.0 °C | -85.0 - -5.80 °F | Average value: -59.2 °C Grade Count:37 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:154 |
| Flammability Test | 37.0 - 54.0 | 37.0 - 54.0 | Average value: 45.2 Grade Count:15 |
| Oxygen Index | 27.0 % | 27.0 % | Average value: 27.0 % Grade Count:4 |
| Ring & Ball Softening Point | 128 - 135 °C | 262 - 275 °F | Average value: 131 °C Grade Count:4 |
| Optical Properties | Metric | English | Comments |
| Haze | 3.70 - 15.0 % | 3.70 - 15.0 % | Average value: 9.16 % Grade Count:21 |
| Transmission, Visible | 82.0 - 91.0 % | 82.0 - 91.0 % | Average value: 89.9 % Grade Count:84 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 140 - 280 °C | 284 - 536 °F | Average value: 208 °C Grade Count:387 |
| Nozzle Temperature | 175 - 249 °C | 347 - 480 °F | Average value: 187 °C Grade Count:9 |
| Die Temperature | 140 - 249 °C | 284 - 480 °F | Average value: 191 °C Grade Count:3 |
| Melt Temperature | 149 - 371 °C | 300 - 700 °F | Average value: 195 °C Grade Count:109 |
| Mold Temperature | 10.0 - 149 °C | 50.0 - 300 °F | Average value: 44.5 °C Grade Count:252 |
| Drying Temperature | 51.7 - 135 °C | 125 - 275 °F | Average value: 75.0 °C Grade Count:248 |
| Dry Time | 2.00 - 80.0 hour | 2.00 - 80.0 hour | Average value: 3.83 hour Grade Count:116 |
| Moisture Content | 0.0300 - 0.150 % | 0.0300 - 0.150 % | Average value: 0.0437 % Grade Count:68 |
| Dew Point | -31.7 - -17.8 °C | -25.0 - 0.000 °F | Average value: -18.1 °C Grade Count:42 |
| Injection Pressure | 1.38 - 138 MPa | 200 - 20000 psi | Average value: 76.1 MPa Grade Count:91 |
| Back Pressure | 0.172 - 0.689 MPa | 25.0 - 100 psi | Average value: 0.349 MPa Grade Count:10 |
| Screw Speed | 25.0 - 100 rpm | 25.0 - 100 rpm | Average value: 52.5 rpm Grade Count:10 |