- 密度 [g/cm3]: 1.21
- 吸水率 [%]: 0.27
- 缺口沖擊強度: 0.427
- 拉伸強度 [MPa]: 91.0
- 斷裂伸長率 [%]: 124
- 彎曲模量 [MPa]: 3.10
- 硬度: 116.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in3 | ASTM D792 |
| Water Absorption | 0.27 % @Time 86400 sec | 0.27 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 3.17 mm | 0.0080 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength, Yield | 91.0 MPa | 13200 psi | ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm | 0.800 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 46.8 μm/m-°C | 26.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |