- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 2.3
- 缺口沖擊強度: 0.961
- 拉伸強度 [MPa]: 77.9
- 彎曲模量 [MPa]: 3.17
- 硬度: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ASTM D792 |
| Water Absorption | 2.3 % @Time 86400 sec | 2.3 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0019 cm/cm @Thickness 3.17 mm | 0.0019 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 77.9 MPa | 11300 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 150 MPa | 21700 psi | ASTM D790 |
| Flexural Modulus | 3.17 GPa | 460 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm | 1.80 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 73.8 μm/m-°C | 41.0 μin/in-°F | ASTM D696 |
| Melting Point | 146 °C | 295 °F | |
| Maximum Service Temperature, Inert | 130 °C | 266 °F | ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |