- 密度 [g/cm3]: 1.26
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 1.07
- 拉伸強度 [MPa]: 117.0
- 彎曲模量 [MPa]: 5.31
- 硬度: 127.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in3 | ASTM D792 |
| Water Absorption | 0.30 % @Time 86400 sec | 0.30 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 3.17 mm | 0.0070 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 127 | 127 | ASTM D785 |
| Tensile Strength, Yield | 117 MPa | 17000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 162 MPa | 23500 psi | ASTM D790 |
| Flexural Modulus | 5.31 GPa | 770 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm | 2.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 54.0 μm/m-°C | 30.0 μin/in-°F | ASTM D696 |
| Melting Point | 310 °C | 590 °F | |
| Maximum Service Temperature, Inert | 160 °C | 320 °F | ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | Unannealed; ASTM D648 |