- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 3.1
- 缺口沖擊強度: 0.801
- 拉伸強度 [MPa]: 124.0
- 彎曲模量 [MPa]: 5.52
- 硬度: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in3 | ASTM D792 |
| Water Absorption | 3.1 % @Time 86400 sec | 3.1 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0075 cm/cm @Thickness 3.17 mm | 0.0075 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 124 MPa | 18000 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 172 MPa | 25000 psi | ASTM D790 |
| Flexural Modulus | 5.52 GPa | 800 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 3.17 mm | 1.50 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 64.8 μm/m-°C | 36.0 μin/in-°F | ASTM D696 |
| Melting Point | 146 °C | 295 °F | |
| Maximum Service Temperature, Inert | 160 °C | 320 °F | ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |