- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.65
- 缺口沖擊強度: 9.61
- 拉伸強度 [MPa]: 75.8
- 彎曲模量 [MPa]: 2.62
- 硬度: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in3 | ASTM D792 |
| Water Absorption | 0.65 % @Time 86400 sec | 0.65 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm @Thickness 3.17 mm | 0.018 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 75.8 MPa | 11000 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 128 MPa | 18500 psi | ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | ASTM D790 |
| Izod Impact, Notched | 9.61 J/cm @Thickness 3.17 mm | 18.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 68.4 μm/m-°C | 38.0 μin/in-°F | ASTM D696 |
| Melting Point | 154 °C | 310 °F | |
| Maximum Service Temperature, Inert | 160 °C | 320 °F | ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Unannealed; ASTM D648 |