- 密度 [g/cm3]: 1.41
- 缺口沖擊強度: 1.38
- 彎曲模量 [MPa]: 10.78
- 熱變形溫度 [℃]: 219.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in3 | ASTM D 792 |
| 1.42 g/cc | 0.0513 lb/in3 | ISO 1183 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 171 MPa | 24800 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 3.3 % | 3.3 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 12.42 GPa | 1801 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 183 MPa | 26500 psi | ISO 178 |
| 255 MPa | 37000 psi | brk, 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 10.78 GPa | 1564 ksi | 2 mm/min; ISO 178 |
| 10.79 GPa | 1565 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 1.38 J/cm @Temperature 23.0 °C | 2.59 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 11.21 J/cm @Temperature 23.0 °C | 21.00 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C @Thickness 3.20 mm | 426 °F @Thickness 0.126 in | unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 207 °C @Thickness 3.20 mm | 405 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |