- 密度 [g/cm3]: 1.17
- 缺口沖擊強度: 0.37
- 拉伸強度 [MPa]: 45.0
- 彎曲模量 [MPa]: 2.75
- 熱變形溫度 [℃]: 193.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in3 | ASTM D792 |
| 1.17 g/cc | 0.0423 lb/in3 | ISO 1183 | |
| Moisture Absorption | 0.300 % | 0.300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Time 86400 sec | 0.010 in/in @Time 24.0 hour | ASTM D955 |
| 0.010 cm/cm @Time 86400 sec | 0.010 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm @Time 86400 sec | 0.018 in/in @Time 24.0 hour | ASTM D955 |
| 0.018 cm/cm @Time 86400 sec | 0.018 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ASTM D638 |
| 50.0 MPa | 7250 psi | ISO 527 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D638 |
| 50.0 MPa | 7250 psi | ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| 2.3 % | 2.3 % | ISO 527 | |
| Elongation at Yield | 1.8 % | 1.8 % | ASTM D638 |
| 2.3 % | 2.3 % | ISO 527 | |
| Tensile Modulus | 3.31 GPa | 480 ksi | 1 mm/min; ISO 527 |
| 3.44 GPa | 499 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 76.0 MPa | 11000 psi | ISO 178 |
| 103 MPa | 14900 psi | ASTM D790 | |
| Flexural Modulus | 2.75 GPa | 399 ksi | ASTM D790 |
| 3.00 GPa | 435 ksi | ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.52 J/cm | 6.59 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 | 1.90 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m2 | 15.2 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 1.00 J | 0.738 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.41 | 0.41 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.26 | 0.26 | ASTM D3702 Modified |
| K (wear) Factor | 22.2 x 10-8 mm3/N-M | 11.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 84.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 46.7 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 84.6 μm/m-°C @Temperature -40.0 - 40.0 °C | 47.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 63.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 35.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 63.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 35.0 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 193 °C | 379 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 203 °C @Thickness 3.20 mm | 397 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 118 °C @Thickness 3.20 mm | 244 °F @Thickness 0.126 in | unannealed; ASTM D648 | |