- 密度 [g/cm3]: 1.16
- 缺口沖擊強度: 0.42
- 拉伸強度 [MPa]: 48.0
- 彎曲模量 [MPa]: 1.37
- 熱變形溫度 [℃]: 165.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | ISO 1183 |
| 1.17 g/cc | 0.0423 lb/in3 | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.30 % @Time 86400 sec | 0.30 % @Time 24.0 hour | 50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.019 - 0.021 cm/cm @Time 86400 sec | 0.019 - 0.021 in/in @Time 24.0 hour | ASTM D 955 |
| 0.020 cm/cm @Time 86400 sec | 0.020 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.021 - 0.023 cm/cm @Time 86400 sec | 0.021 - 0.023 in/in @Time 24.0 hour | ASTM D 955 |
| 0.022 cm/cm @Time 86400 sec | 0.022 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ASTM D 638 |
| 51.0 MPa | 7400 psi | ISO 527 | |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D 638 |
| 51.0 MPa | 7400 psi | ISO 527 | |
| Elongation at Break | 11.9 % | 11.9 % | ASTM D 638 |
| 14 % | 14 % | ISO 527 | |
| Elongation at Yield | 13.8 % | 13.8 % | ISO 527 |
| 16.5 % | 16.5 % | ASTM D 638 | |
| Tensile Modulus | 2.06 GPa | 299 ksi | 50 mm/min; ASTM D 638 |
| 2.29 GPa | 332 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Modulus | 1.37 GPa | 199 ksi | ASTM D 790 |
| 2.00 GPa | 290 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm @Temperature 23.0 °C | 0.787 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 8.33 J/cm @Temperature 23.0 °C | 15.6 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 46.0 kJ/m2 @Temperature 23.0 °C | 21.9 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 15.0 J | 11.1 ft-lb | Multiaxial Impact; ISO 6603 |
| 3.00 J @Temperature 23.0 °C | 2.21 ft-lb @Temperature 73.4 °F | Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.19 | 0.19 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.15 | 0.15 | ASTM D 3702 Modified |
| K (wear) Factor | 6.04 x 10-8 mm3/N-M | 3.00 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 98.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 54.4 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 99.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 55.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 97.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 53.9 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 97.2 μm/m-°C @Temperature -40.0 - 40.0 °C | 54.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 163 °C @Thickness 3.20 mm | 325 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 57.0 °C @Thickness 3.20 mm | 135 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |