- 密度 [g/cm3]: 1.33
- 缺口沖擊強度: 1.24
- 拉伸強度 [MPa]: 156.0
- 斷裂伸長率 [%]: 239
- 彎曲模量 [MPa]: 7.93
- 熱變形溫度 [℃]: 219.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Density | 1.33 g/cc | 0.0480 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.370 % | 0.370 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm @Time 86400 sec | 0.0010 - 0.0040 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec | 0.0090 - 0.020 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 156 MPa | 22600 psi | Type I, 5 mm/min; ASTM D638 |
| 157 MPa | 22800 psi | 5 mm/min; ISO 527 | |
| 176 MPa | 25500 psi | ASTM D638 | |
| Tensile Strength, Yield | 156 MPa | 22600 psi | Type I, 5 mm/min; ASTM D638 |
| 157 MPa | 22800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 |
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 |
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 9.60 GPa | 1390 ksi | 1 mm/min; ISO 527 |
| 9.97 GPa | 1450 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 227 MPa | 32900 psi | ISO 178 |
| 238 MPa | 34500 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| 268 MPa | 38900 psi | ASTM D790 | |
| Flexural Yield Strength | 239 MPa | 34700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.93 GPa | 1150 ksi | 2 mm/min; ISO 178 |
| 8.32 GPa | 1210 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 8.90 GPa | 1290 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.24 J/cm | 2.32 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.8 J/cm | 20.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m2 | 5.23 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m2 | 30.9 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C | 7.38 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 35.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 19.4 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 114 μm/m-°C @Temperature -30.0 - 30.0 °C | 63.3 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 222 °C @Thickness 3.20 mm | 432 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 214 °C @Thickness 3.20 mm | 417 °F @Thickness 0.126 in | unannealed; ASTM D648 | |