- 熔體流動速率 [g/10min]: 60.0
- 密度 [g/cm3]: 1.03
- 缺口沖擊強度: 0.29
- 拉伸強度 [MPa]: 20.0
- 彎曲模量 [MPa]: 0.520
- 熱變形溫度 [℃]: 60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in3 | ASTM D792 |
| Melt Flow | 60 g/10 min @Load 1.00 kg, Temperature 190 °C | 60 g/10 min @Load 2.20 lb, Temperature 374 °F | ASTM D1238R |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | >= 27.0 MPa | >= 3920 psi | ASTM D638 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Elongation at Break | >= 300 % | >= 300 % | ASTM D638 |
| Flexural Strength | 23.0 MPa | 3340 psi | ASTM D790 |
| Flexural Modulus | 0.520 GPa | 75.4 ksi | ASTM D790 |
| Izod Impact, Notched | 0.290 J/cm | 0.543 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 145 °C | 293 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |