- 密度 [g/cm3]: 1.33
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.747
- 拉伸強度 [MPa]: 114.0
- 斷裂伸長率 [%]: 145
- 彎曲模量 [MPa]: 6.55
- 硬度: 118.0
- 熱變形溫度 [℃]: 144.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in3 | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm | 0.0030 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Yield Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 6.55 GPa | 950 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 3.17 mm | 1.40 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 3.20 J/cm @Thickness 3.17 mm | 6.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | ASTM D257 |
| Surface Resistance | 100000 ohm | 100000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 19.8 μm/m-°C | 11.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 144 °C | 292 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 283 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-2 | V-2 | |